Riblene® FF 30
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Riblene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ekdO1x_Riblene-FF-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Riblene FF 30 is a high molecular weight low density polyethylene (LDPE), suitable for blown film extrusion. Riblene FF 30 is characterised by a good melt strength leading to a good bubble stability during extrusion. Films manufactured by Riblene FF 30 are easily heat shrinkable and characterised by good optical and mechanical properties. Main Application Riblene FF 30 is recommended for the production of shrink film for medium and light loads, for lamination film and for blend. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 70 | µm | |
| Film Thickness - Recommended / Available | 30 to 120 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 70 µm, Blown Film | 180 | MPa | |
| 1% Secant, TD : 70 µm, Blown Film | 190 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 70 µm, Blown Film | 10.0 | MPa | |
| TD : Yield, 70 µm, Blown Film | 11.0 | MPa | |
| MD : Break, 70 µm, Blown Film | 22.0 | MPa | |
| TD : Break, 70 µm, Blown Film | 19.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 70 µm, Blown Film | 380 | % | |
| TD : Break, 70 µm, Blown Film | 600 | % | |
| Dart Drop Impact 1(70 µm, Blown Film) | 180 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 70.0 µm | 45.0 | kN/m | |
| TD : 70.0 µm | 60.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 95.0 | °C | ISO 306/A |
| Melting Temperature | 113 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 70.0 µm, Blown Film) | 65 | ASTM D2457 | |
| Haze (70.0 µm, Blown Film) | 8.0 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 to 200 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP GP1001FC | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| DENKA EVA TEX 75 | Denka Company Limited | EVA | DENKA EVA TEX |
| Gallonprene® GP410-6501 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| KOPLA PC KBG1030 | KOPLA Co., Ltd. | PBT | KOPLA PC |
| Karina BLACK PVC COMPOUND -E 70900-48/ 1-E-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |