| OP-PEI 1000 is a polyetherimide (PEI) material,. This product is available in North America and is processed by injection molding. The main characteristics of OP-PEI 1000 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 - 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 103 | MPa | ASTM D638 |
| Fracture | 103 | MPa | ASTM D638 |
| Flexural Modulus | 3240 | MPa | ASTM D790 |
| Flexural Strength | 145 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (4°C) | 53 | J/m | ASTM D256 |
| Dart Drop Impact | 36.2 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 204 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 196 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | V-0 | UL 94 | |
| 3.18 mm | V-0 | UL 94 |
| Additional Information |
|---|
| Melt Mass - Flow Rate (MFR), ASTM D1238, 190°C/ 2.16kg:10 to 30 g/10min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 143 - 149 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Rear Temperature | 332 - 399 | °C | |
| Middle Temperature | 338 - 399 | °C | |
| Front Temperature | 343 - 399 | °C | |
| Processing (Melt) Temp | 338 - 399 | °C | |
| Mold Temperature | 107 - 177 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XCW-8880N | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Aaroprene® ATPR 1000 60A | Aaron Industries Corp. | TPE | Aaroprene® |
| Baypreg® F 315 (10 mm Glass Mat Reinforced Sandwich) | Covestro - PUR | PUR, Unspecified | Baypreg® |
| FHR EPS 54-3654 | Flint Hills Resources, LP | PS (EPS) | FHR EPS |
| Ecollent™ PC | Lucent Polymers, Inc. | PC | Ecollent™ |