Zytel® FG408L NC010
| Category: | Nylon 66 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eiaYvl_Zytel-FG408L-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced, Toughened, Polyamide 66 with Developed for Food Contact Applications |
| General Information | |
|---|---|
| Additive |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.09 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.5 | -- | % | |
| Flow | 1.5 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 7.0 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 2.2 | -- | % | |
| Viscosity Number | 150 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2200 | 1100 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 61.0 | 43.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 6.0 | 26 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 35 | > 50 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 950 | MPa | |
| 1000 hr | -- | 840 | MPa |
| Films | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Elongation - MD (Yield) | 6.0 | -- | % | ISO 527-3 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 15 | 8.0 | kJ/m² | |
| 23°C | 15 | 25 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 155 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 66.0 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 210 | -- | °C | ISO 306/B50 |
| Melting Temperature 1 | 263 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.3E-4 | -- | cm/cm/°C | |
| Transverse | 1.3E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 34 | -- | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 3.20 | 7.00 | ||
| 1 MHz | 2.90 | 3.70 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.020 | 0.15 | ||
| 1 MHz | 0.020 | 0.050 | ||
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| Oxygen Index | 19 | -- | % | ISO 4589-2 |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Melt Density | 0.950 | -- | g/cm³ | |
| Specific Heat Capacity of Melt | 2600 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.16 | -- | W/m/K |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sevrene® 3582-80A | Vi-Chem Corporation | TPE | Sevrene® |
| Nucrel® 699 | DuPont Packaging & Industrial Polymers | EMAA | Nucrel® |
| DEXFLEX® 1011E | LyondellBasell Industries | TPO (POE) | DEXFLEX® |
| KOPET® KP133G30 | Kolon Plastics, Inc. | PET | KOPET® |
| Karina BLACK PVC COMPOUND -E 70900-48/ 1-E-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |