LNP™ THERMOTUF™ WF006I compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOTUF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eiYaP2_LNPTHERMOTUFWF006Icompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOTUF WF006I is a compound based on Polybutylene Terephalate resin containing Glass Fiber. Added features of this material include: High Impact. Also known as: LNP* THERMOTUF* Compound WF-1006 HI Product reorder name: WF006I |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.49 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.20 - 0.40 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7600 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 82.0 | MPa | ISO 527-2/5 |
| Fracture | 101 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.6 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 7000 | MPa | ISO 178 |
| Flexural Stress | 160 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 3(23°C) | 13 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 55 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, unannealed, 64.0mm span | 218 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 190 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.6E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PC 11 N | Plastcom | PP Copolymer | SLOVALEN® |
| Bynel® 21E830 | DuPont Packaging & Industrial Polymers | EA | Bynel® |
| TECHNYL® A 218 V25 BLACK 21 | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |
| MARPOL® P1902 | Marco Polo International, Inc. | POP | MARPOL® |
| 3M™ Dyneon™ PTFE Compound APNV063 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |