Advanced Composites TX-35
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Advanced Composites, Inc. |
| Trademark: | Advanced Composites |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eiOvNX_Advanced-Composites-TX-35.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Advanced Composites TX-35 is a polypropylene impact copolymer (PP Impact Copoly) product,. It is available in North America. Typical application areas are: automotive industry. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 35 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 1.5 - 1.8 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 25.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 500 | % | ASTM D638 |
| Flexural Modulus 3 | 1220 | MPa | ASTM D790 |
| Flexural Strength 4 | 31.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 70 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 110 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 171 | °C | |
| Middle Temperature | 179 - 199 | °C | |
| Front Temperature | 216 | °C | |
| Nozzle Temperature | 204 | °C | |
| Processing (Melt) Temp | 185 - 227 | °C | |
| Mold Temperature | 26.7 - 43.3 | °C | |
| Injection Rate | Slow-Moderate | ||
| Cushion | 5.00 - 10.0 | mm |
| Injection instructions |
|---|
| Injection Pressure: 20 to 60% oof machine capacityScrew RPM: 1 to 2 secs before mold open |
| Note Message | |
|---|---|
| 1 . | 10 mm/min |
| 2 . | 10 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds PP-3235 | Ravago Manufacturing Americas, LLC | PP Copolymer | Ravago Compounds |
| Sindustris PBT TE5101 | Sincerity Australia Pty Ltd. | PC+PBT | Sindustris PBT |
| Topilene® HB240P | Hyosung Corporation | PP Impact Copolymer | Topilene® |
| EPIMIX PBT GFR 10 NC | EPSAN Plastik SAN. ve TiC. A.S. | PBT | EPIMIX |
| LNP™ THERMOCOMP™ LF003 compound | SABIC Innovative Plastics | PEEK | LNP™ THERMOCOMP™ |