SEETEC LDPE BF415
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | SEETEC LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ehqhxz_SEETEC-LDPE-BF415.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Application
Feature
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.922 to 0.926 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.6 to 2.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 2% Secant 2 | 118 | MPa | ASTM D638 |
| Tensile Strength 3 | ASTM D638 | ||
| Across Flow : Break | 23.5 | MPa | |
| Flow : Break | 25.5 | MPa | |
| Break | 12.3 | MPa | |
| Tensile Elongation 4 | |||
| Break 5 | 550 | % | ASTM D638 |
| Break 6 | 300 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dart Drop Impact | 55 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 400 | g | |
| TD | 180 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 92.0 | °C | ASTM D1525 |
| Peak Melting Temperature 7 | 112 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 95 | ASTM D2457 | |
| Haze | 5.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Condition: 23°C |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| 4 . | 500 mm/min |
| 5 . | Across Flow |
| 6 . | Flow |
| 7 . | Condition: 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAFORM® 9 F EC | A. Schulman Europe | Acetal (POM) Copolymer | SCHULAFORM® |
| SLOVAMID® 6 BT LS | Plastcom | Nylon 6 | SLOVAMID® 6 |
| Surlyn® 8940-E | DuPont Packaging & Industrial Polymers | Ionomer | Surlyn® |
| HIVOREX 5200B | Lotte Chemical Corporation | HDPE | HIVOREX |
| MARPOL® COPP 20.4 | Marco Polo International, Inc. | PP Impact Copolymer | MARPOL® COPP |