IROGRAN® A 70 H 4714 M
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Huntsman Corporation |
| Trademark: | IROGRAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ehASf7_IROGRAN-A-70-H-4714-M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
IROGRAN A 70 H 4714 M is a soft polyester based thermoplastic polyurethane intended for injection moulding applications. IROGRAN A 70 H 4714 M is part of the HUNTSMAN injection moulding product range. It is processable at low temperatures and offers a specially designed, flexible material suitable for mouldings. PERFORMANCE FEATURES
|
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.16 | g/cm³ | ASTM D792, DIN 53479 |
| Melt Volume-Flow Rate (MVR) (190°C/5.0 kg) | 30.0 | cm³/10min | |
| Molding Shrinkage - Flow (Injection Molded) | 0.90 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| Shore A, Injection Molded | 68 | ASTM D2240, DIN 53505 | |
| Shore D, Injection Molded | 20 | ASTM D2240 | |
| Shore D, Injection Molded | 21 | DIN 53505 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion 2 | 30 | mm³ | DIN 53516 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| TMA 3 | Internal Method | ||
| High : 635.0 µm | 165 | °C | |
| Low : 635.0 µm | 120 | °C |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 4 | DIN 53504 | ||
| 100% Strain, 0.635 mm | 3.40 | MPa | |
| 300% Strain, 0.635 mm | 7.00 | MPa | |
| Tensile Stress 5(Break, 0.635 mm) | 45.0 | MPa | DIN 53504 |
| Tensile Elongation 6(Break, 0.635 mm) | 770 | % | DIN 53504 |
| Tear Strength 7(0.635 mm) | 45 | kN/m | DIN 53515 |
| Compression Set 8 | ASTM D395, DIN 53517 | ||
| 23°C, 24 hr | 34 | % | |
| 70°C, 24 hr | 48 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 | °C | |
| Hot Air Dryer | 90.0 | °C | |
| Drying Time | |||
| -- | 3.0 | hr | |
| Hot Air Dryer | 3.0 | hr | |
| Dew Point | -30.0 | °C | |
| Hopper Temperature | 175 | °C | |
| Rear Temperature | 180 | °C | |
| Middle Temperature | 180 | °C | |
| Front Temperature | 180 | °C | |
| Nozzle Temperature | 180 | °C |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | Injection Molded |
| 3 . | Extruded Film |
| 4 . | Extruded Film |
| 5 . | Extruded Film |
| 6 . | Extruded Film |
| 7 . | Extruded Film |
| 8 . | Injection Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU C665MNAT | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Keltan® ECO 8550 | LANXESS Buna GmbH | EPDM | Keltan® |
| INNOPOL® PP CS 2-4630 FR | Inno-Comp Ltd. | PP Impact Copolymer | INNOPOL® PP |
| LNP™ THERMOCOMP™ OF008E compound | SABIC Innovative Plastics | PPS, Linear | LNP™ THERMOCOMP™ |
| Sylvin 9724-80FUV Green 3179 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |