Hytrel® 4068FG
| Category: | TPC-ET , THERMOPLASTIC POLYESTER ELASTOMER |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Hytrel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | egtu87_Hytrel-4068FG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40 Shore D High Performance Polyester Elastomer Developed for Food Contact Applications |
| General Information | |
|---|---|
| Additive |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.11 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/2.16 kg) | 8.5 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (220°C/2.16 kg) | 9.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.80 | % | |
| Flow | 0.80 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 2.00 mm | 0.70 | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.30 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 37 | ||
| Shore D, 15 sec | 33 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 45.0 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Break | 29.0 | MPa | |
| 5.0% Strain | 2.40 | MPa | |
| 10% Strain | 3.50 | MPa | |
| 50% Strain | 6.70 | MPa | |
| Tensile Strain (Break) | > 300 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 800 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 28.0 | MPa | |
| 1000 hr | 21.0 | MPa | |
| Flexural Modulus | 47.0 | MPa | ISO 178 |
| Abrasion Resistance | 180 | mm³ | ISO 4649 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Effective Thermal Diffusivity | 0.0544 | cSt |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | ISO 34-1 | ||
| Across Flow | 100 | kN/m | |
| Flow | 100 | kN/m |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | No Break | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Tensile Impact Strength (23°C) | 145 | kJ/m² | ISO 8256/1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature 1 | -55.0 | °C | ISO 11357-2 |
| Melting Temperature 2 | 193 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 2.3E-4 | cm/cm/°C | |
| Transverse | 2.3E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electric Strength | 18 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 4.80 | ||
| 1 MHz | 4.70 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAN 3O 42 | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| Sinpolene HFR8018 | Teknor Apex Asia Pacific PTE. LTD. | TP, Unspecified | Sinpolene |
| Moplen EP545L | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| HiFill® PEEK CF30 HF | Techmer Engineered Solutions | PEEK | HiFill® |
| Karina CLEAR PVC COMPOUND -E 800/208-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |