RTP 199 X 124807
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | efPIhP_RTP-199-X-124807.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame Retardant - UV Stabilized |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.4 to 2.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 896 | MPa | ASTM D638 |
| Tensile Strength | 22.8 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 10 | % | ASTM D638 |
| Flexural Modulus | 1030 | MPa | ASTM D790 |
| Flexural Strength | 30.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 120 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | No Break | ASTM D4812 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-0 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 191 to 232 | °C | |
| Mold Temperature | 32.2 to 65.6 | °C | |
| Injection Pressure | 68.9 to 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TORZEN® T2000HSL BK20 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| BESTNYL SE35VI01AH | Triesa Plastics | Nylon 66 | BESTNYL |
| Cellophane™ 345DMS | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| K-Bin Rigid PVC KBD-5001 | K-Bin, Inc. | PVC, Unspecified | K-Bin Rigid PVC |
| Piolen® P B50A19 | PiO Kunststoffe GmbH & Co KG | PP Homopolymer | Piolen® P |