LG ABS XR407E
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | efCvtL_LG-ABS-XR407E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Heat Resistance Applicaiton Electric & Electronic Housing (MWO Frame, DVD inner part etc.) |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 45.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 20 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2450 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 74.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 78 | J/m | |
| -30°C, 6.40 mm | 69 | J/m | |
| 23°C, 3.20 mm | 180 | J/m | |
| 23°C, 6.40 mm | 170 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 113 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 105 | °C | |
| Vicat Softening Temperature | 114 | °C | ASTM D1525 5 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI Str | 60.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.070 | % | |
| Rear Temperature | 180 to 200 | °C | |
| Middle Temperature | 200 to 220 | °C | |
| Front Temperature | 220 to 230 | °C | |
| Nozzle Temperature | 220 to 230 | °C | |
| Processing (Melt) Temp | 190 to 210 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 0.981 to 2.94 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULADUR® A GB 30 SCHWARZ | A. Schulman Europe | PBT | SCHULADUR® |
| MORETEC™ 0158N | Prime Polymer Co., Ltd. | LLDPE | MORETEC™ |
| NORYL™ HM4025H resin | SABIC Innovative Plastics Asia Pacific | PPE+PS | NORYL™ |
| ECP 121/1015 | TBA Electro Conductive Products Ltd. | EVA | ECP |
| Sylvin 8260-85 Brown 7487 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |