Durethan® BM 430 H2.0 901510
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eenEel_DurethanBM430H20901510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 30 % mineral, injection molding, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.37 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 2577 | |||
| Vertical flow direction : 280°C, 2.00mm 1 | 1.1 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 2.00mm 2 | 0.20 | -- | % | ISO 2577 |
| Flow direction : 280°C, 2.00mm 3 | 1.2 | -- | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 2.00mm 4 | 0.30 | -- | % | ISO 2577 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 2.0 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 7.1 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 4700 | 1450 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 70.0 | 35.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 5.0 | > 100 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 4500 | 1590 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% strain, 23°C | 115 | 35.0 | MPa | ISO 178/A |
| 23°C 6 | 120 | 48.0 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 5.0 | 7.8 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GHR, 14-040, MD30 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| 23°C | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 60 | 50 | kJ/m² | ISO 179/1eU |
| 23°C | 75 kJ/m² | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| 23°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 50 | 55 | kJ/m² | ISO 180/1U |
| 23°C | 65 kJ/m² | No Break | ISO 180/1U | |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 1.50 | -- | J | ISO 6603-2 |
| 23°C | 2.50 | -- | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | |||
| -30°C | 820 | -- | N | ISO 6603-2 |
| 23°C | 1400 | -- | N | ISO 6603-2 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 175 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 75.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 8 | 222 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 8.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 7.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SIMONA® PVDF-GK | SIMONA AMERICA, Inc. | PVDF | SIMONA® |
| TEREZ PBT 6750/2 T GK 20 | TER HELL PLASTIC GMBH | PBT | TEREZ PBT |
| COPYLENE® CM038LN | Phillips 66 | PP Impact Copolymer | COPYLENE® |
| EPO-TEK® EK1000-1MP | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Hostacom TRC 104N | LyondellBasell Industries | TPO (POE) | Hostacom |