SPESIN® KP213G30BL
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Kolon Plastics, Inc. |
| Trademark: | SPESIN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eePW9B_SPESIN-KP213G30BL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SPESIN® KP213G30BL is a Polybutylene Terephthalate (PBT) product filled with 30% glass fiber. It is available in Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 to 1.0 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 137 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 5.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 8340 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 211 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 88 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648A | ||
| 0.45 MPa, Unannealed | 220 | °C | |
| 1.8 MPa, Unannealed | 205 | °C | |
| Peak Melting Temperature | 224 | °C | ASTM D3418 |
| CLTE - Flow | 4.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 30 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.20 | ASTM D150 | |
| Arc Resistance | 120 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultralloy™ 202 | Hapco Inc. | TP, Unspecified | Ultralloy™ |
| DINALON® B2S25 V2-7035 | Grupo Repol | Nylon 6 | DINALON® |
| Kuraray Poval® CM-318 | Kuraray Co., Ltd. | PVOH | Kuraray Poval® |
| IROGRAN® A 91 P 4945 | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| LOTTMER HS-040DB | Lotte Chemical Corporation | TPE | LOTTMER |