RTP 800 GB 20 TFE 15
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | edL2bI_RTP-800-GB-20-TFE-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.64 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 2.0 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 107 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ASTM D638 |
| Tensile Strength | 41.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638 |
| Flexural Modulus | 2900 | MPa | ASTM D790 |
| Flexural Strength | 68.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 480 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 163 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 116 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm, RTP Tested) | HB | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 30mil/in. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 191 - 210 | °C | |
| Middle Temperature | 191 - 210 | °C | |
| Front Temperature | 191 - 210 | °C | |
| Mold Temperature | 93.3 - 121 | °C | |
| Injection Pressure | 68.9 - 103 | MPa | |
| Back Pressure | 0.172 - 0.345 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP PP PPH2CF2-Black | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| APEX® 2585-H | Teknor Apex Company | PVC, Flexible | APEX® |
| Epoxies, Ect. 20-3035 (Cat.30) | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| Kingfa API-3307 | Kingfa | PP, Unspecified | Kingfa |
| LUVOCOM® 1-8642 | LEHVOSS Group | Nylon 66 | LUVOCOM® |