AFFINITY™ PL 1840G
| Category: | POP , Polyolefin Plastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | AFFINITY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | edCTro_AFFINITY-PL-1840G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
AFFINITY* PL 1840G Polyolefin Plastomer (POP) is produced via INSITE* Technology. It is an ethylene alpha-olefin resin designed to provide blown film with low temperature sealability, good puncture resistance, optics and organoleptic properties. It also has excellent compatibility with other polyolefins, allowing efficient blending and coextrusion.
Applications:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.909 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Film Puncture Energy (51 µm) | 9.16 | J | Internal method |
| Film Puncture Force (51 µm) | 93.0 | N | Internal method |
| Film Puncture Resistance (51 µm) | 25.2 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 51 µm | 123 | MPa | ASTM D882 |
| 2% secant, TD : 51 µm | 123 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 8.76 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 8.07 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 47.8 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 45.4 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 620 | % | ASTM D882 |
| TD : Fracture, 51 µm | 580 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | > 830 | g | ASTM D1709B |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 51 µm | 560 | g | ASTM D1922 |
| TD : 51 µm | 840 | g | ASTM D1922 |
| Seal Initiation Temperature 2(51 µm) | 92.8 | °C | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 106 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 50.8 µm) | 128 | ASTM D2457 | |
| Clarity (50.8 µm) | 63.0 | ASTM D1746 | |
| Haze (50.8 µm) | 2.5 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 221 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：2.5 英寸 (63.5 mm)；24:1 L/D 螺杆类型：DSB11 模具间隙：70 密尔 (1.8 mm) 熔体温度：429°F (220°C) 输出：模具周长的 6 磅/小时/英寸 模具直径：6 英寸 放大比：2.5:1 螺杆速度：40 rpm |
| Note Message | |
|---|---|
| 1 . | Modified rectangular test piece. |
| 2 . | Achieve a temperature of 2 psig (8.8 N/25.4mm) heat seal strength. Heat seal strength, Topwave HT tester 0.5 S holding pressure, 40 psi pressure, pulling speed 10 inches/min (250 mm/s). |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 201 FR UV | RTP Company | Nylon 66 | RTP |
| TECHNYL® A 52G1 MX20 BLACK 61 | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| TOTAL Polypropylene PPH 4026 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| ADENE NCWE | A.D. Compound spa | PP Homopolymer | ADENE |
| DURACON® NW-02 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer+PE | DURACON® |