Retpol® 200 GF HS
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | edC6Zz_Retpol-200-GF-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Extron 200 GF HS is a 20% glass fibre reinforced homopolymer polypropylene compound. It is a low flow injection moulding grade developed for rigid components requiring high heat deflection temperatures and low mould shrinkages. It is stabilized to meet automotive heat ageing requirements of 500hrs at 150°C. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.20 to 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.00 mm) | 111 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 79 | ||
| Shore D, 15 sec, 3.00 mm | 72 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 59.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 3.0 | % | ASTM D638 |
| Flexural Modulus (3.00 mm) | 3900 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.00 mm) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.00 mm) | 270 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.00 mm | 150 | °C | |
| 1.8 MPa, Unannealed, 3.00 mm | 130 | °C | |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 4.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zhongfa PP pp3 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| Gallonprene® GP100-7002 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Garaflex™ E 4762-A5 NAT LCF | AlphaGary | TPE | Garaflex™ E |
| Hangzhou Jinxin VMCPP Film | Hangzhou Jinxin Filming Packaging Co., Ltd. | Film, PP | Hangzhou Jinxin |
| Hostacom BFR | LyondellBasell Industries | PP Copolymer | Hostacom |