SCHULAMID® 6 GF 15
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eclFhR_SCHULAMID-6-GF-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 15% glass fibre reinforced Polyamide 6 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.23 | -- | g/cm³ | ISO 1183/A |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 174 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5800 | 3000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 120 | 70.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.5 | 15 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 4300 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 170 | -- | MPa | ISO 178 |
| Flexural Strain at Flexural Strength | 6.5 | -- | % | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.0 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 7.0 | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 40 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 45 kJ/m² | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 210 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 200 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 215 | -- | °C | ISO 306/A50 |
| -- | 210 | -- | °C | ISO 306/B50 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | < 100 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.750 mm | HB | -- | IEC 60695-11-10, -20 | |
| 1.50 mm | HB | -- | IEC 60695-11-10, -20 | |
| 3.00 mm | HB | -- | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.50 mm | -- | 650 | °C | IEC 60695-2-12 |
| 3.00 mm | -- | 650 | °C | IEC 60695-2-12 |
| Additional Information |
|---|
| 干燥 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VINIKA® CB88EA | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| Wondel® C CEA | Nanjing Julong Engineering Plastics Co., LTD | PC+PE | Wondel® C |
| North American Santicizer® 148 | Ferro Corporation | Plasticizer | North |
| Nylene® 409 | Custom Resins Group | Nylon 6 | Nylene® |
| Sylvin 8999-70 White 1423 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |