VECTOR® 8508A

Category:	SBS , Styrene Butadiene Styrene Block Copolymer
Manufacturer:	Dexco Polymers LP
Trademark:	VECTOR®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ecU5CC_VECTOR-8508A.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

VECTOR 8508A
Styrene-Butadiene-Styrene (SBS) Block Copolymer

SBS(1) triblock copolymer.

Contains <1% diblock copolymer.

Medium styrene, low modulus copolymer.

Outstanding thermal stability and excellent melt processability.

Supplied as a porous pellet, dusted with talc.

VECTOR styrenic block copolymers find use under certain regulations as articles or as ingredients in articles intended for food contact or medical applications. Please contact your Dexco Polymers agent for a detailed letter of certification or further information.

VECTOR 8508A styrene-butadiene-styrene block copolymer is produced via proprietary sequential anionic polymerization technology from Dexco Polymers LP, a Dow/ExxonMobil Venture. It is not formulated with the antioxidant TNPP (tris(nonylphenyl) phosphite).

It has excellent thermoplastic elastomer properties, melt processability, and physical strength. It has superior melt processability when compared to VECTOR 2518A SBS. It is designed for use as an impact/toughness modifier in styrenics, in elastomeric film applications, and in formulating adhesives.

General Information
Features	Copolymer Food Contact Acceptable Good Processability Good Thermal Stability High Strength Linear Polymer Structure
Uses	Adhesives Film Plastics Modification
Forms	Pellets

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.938	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (200°C/5.0 kg)	1.2	g/10 min	ASTM D1238
Solution Viscosity	400	mPa·s	ASTM D2196
Ash Content	0.8	wt%	ASTM D1416
Styrene Content	29.0	wt%	Internal Method

Elastomers	Nominal Value	Unit	Test Method
Stress Relaxation ¹
Peak Force @ 200% strain (A) : 23°C, 889.0 µm	1.86	MPa
Peak Force @ 500% strain : 23°C, 889.0 µm	6.14	MPa
Ratio (A:B) : 23°C, 889.0 µm	2.74
Relaxation @ 200% strain : 23°C, 889.0 µm	9.1	%
Set after 500% strain : 23°C, 889.0 µm	15	%
Unload @ 50% strain (B) : 23°C, 889.0 µm	0.689	MPa

Additional Information	Nominal Value	Unit	Test Method
Diblock Content	< 1.0	wt%	Internal Method
Volatiles	0.4	wt%	Internal Method

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A, 1 sec)	65		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress ²(300% Strain, 25°C)	3.65	MPa	ASTM D412
Tensile Strength ³(Yield, 25°C)	33.1	MPa	ASTM D412
Tensile Elongation ⁴(Break, 25°C)	1100	%	ASTM D412

Note Message
1 .	Described in US 7,445,831 patent. Tested on roll milled/compression molded plaques (0.035" thick). Tested in the transverse direction at room temperature.
2 .	25 Wt.% in toluene
3 .	25 Wt.% in toluene
4 .	25 Wt.% in toluene

Resin Grade	Manufacturer	Category	Trademark
Manner Flexible PVC X3610	Manner Plastics, L.P.	PVC, Flexible	Manner Flexible PVC
RTP 3204	RTP Company	ETFE	RTP
ESPRENE EPDM 505	Sumitomo Chemical Co., Ltd.	EPDM	ESPRENE EPDM
LNP™ THERMOCOMP™ JF004EXP compound	SABIC Innovative Plastics	PESU	LNP™ THERMOCOMP™
OmniPro™ TPO 6M SCR	OMNI Plastics, LLC	TPO	OmniPro™