TOTAL Polyethylene HDPE XT10B
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eaD0Oe_TOTAL-Polyethylene-HDPE-XT10B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TOTAL Polyethylene HDPE XT10B is a High Density Polyethylene material. It is available in North America. Important attributes of TOTAL Polyethylene HDPE XT10B are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.958 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/21.6 kg | 7.0 | g/10 min | |
| 190°C/5.0 kg | 0.20 | g/10 min | |
| Carbon Black Content | 3 | % | ASTM D1603 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hydrostatic Design Basis | ASTM D2837 | ||
| 23°C | 11.0 | MPa | |
| 60°C | 6.89 | MPa |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cell Classification | 445574C 445576C | ASTM D3350 | |
| Minimum Required Strength | 10.0 | MPa | ISO 9080 |
| PENT | > 1000 | hr | ASTM F1473 |
| Pipe Category | CEC | ASTM D2513 | |
| PPI Recommended Designation | PE 4710 | PPI TR 4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Compression Molded) | 24.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, Compression Molded) | > 500 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Compression Molded) | 1100 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 130 to 132 | °C | ASTM D3417 |
| Note Message | |
|---|---|
| 1 . | Type IV, 51 mm/min |
| 2 . | Type IV, 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® 1003 | Chevron Phillips Chemical Company LLC | LDPE | Marlex® |
| RTP 1301 P-1 | RTP Company | PPS | RTP |
| Siveras™ LX70G35 | Toray Resin Company | LCP | Siveras™ |
| Expandable PS F21B | INEOS Styrenics International SA | PS (EPS) | Expandable PS |
| Sylvin 4250-95 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |