Generic Nylon 6 - Glass Fiber, Long
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eaAIL6_Generic-Nylon-6---Glass-Fiber-Long.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 6 - Glass Fiber, Long This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.35 - 1.69 | g/cm³ | ASTM D792 |
| 23°C | 1.36 - 1.69 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.075 - 0.30 | % | ASTM D955 |
| 23°C | 0.20 - 0.60 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 8360 - 17600 | MPa | ASTM D638 |
| 23°C | 9510 - 22500 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Fracture, 23°C | 155 - 255 | MPa | ISO 527-2 |
| 23°C | 137 - 236 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Fracture, 23°C | 1.5 - 3.3 | % | ASTM D638 |
| Fracture, 23°C | 1.6 - 2.2 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 6500 - 15500 | MPa | ASTM D790 |
| 23°C | 8210 - 19000 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 210 - 354 | MPa | ASTM D790 |
| 23°C | 249 - 405 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 25 - 32 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 210 - 350 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 1300 - 1500 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 207 - 220 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 210 - 220 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 - 110 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 - 0.18 | % | |
| Rear Temperature | 259 - 270 | °C | |
| Middle Temperature | 270 - 274 | °C | |
| Front Temperature | 277 - 285 | °C | |
| Nozzle Temperature | 278 - 295 | °C | |
| Processing (Melt) Temp | 257 - 320 | °C | |
| Mold Temperature | 73.9 - 105 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 6 - Glass Fiber, LongThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resirene READ 9400 RAF | Resirene, S.A. de C.V. | PS (HIPS) | Resirene |
| Supol HR980E | LyondellBasell Industries | PP, Unspecified | Supol |
| Toraypef® 25020 AP1F | Toray Resin Company | Polyolefin, Unspecified | Toraypef® |
| INELEC PCCF10 | Infinity LTL Engineered Compounds | PC | INELEC |
| ULTEM™ 9085 resin | SABIC Innovative Plastics | PEI | ULTEM™ |