NORYL™ RN0712 resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ea2TpB_NORYL-RN0712-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYL RN0712 is an unfilled Post Consumer recycle (PCR) based injection moldable modified polyphenylene ether resin comprising at least 37% PCR styrenic series resin content. Designed for good dimensional stability and high flow, this resin also uses non-chlorinated, non-brominated FR additives with a specific density of 1.1 g/cm^3. NORYL RN0712 may be an excellent material candidate for flat panel TV enclosure applications requiring good rheological properties, heat resistance, hydrolysis resistance and low density. |
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.11 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 280°C/1.2 kg | 12.0 | cm³/10min | |
| 280°C/2.16 kg | 22.0 | cm³/10min |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2470 | MPa | ASTM D638 |
| -- | 2300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 51.0 | MPa | ASTM D638 |
| Yield | 47.0 | MPa | ISO 527-2/50 |
| Break 3 | 50.0 | MPa | ASTM D638 |
| Break | 49.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 3.5 | % | ASTM D638 |
| Yield | 3.0 | % | ISO 527-2/50 |
| Break | 10 | % | Internal Method |
| Break | 7.0 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 5 | 2300 | MPa | ASTM D790 |
| -- 6 | 2250 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 77.0 | MPa | ISO 178 |
| Break, 50.0 mm Span 7 | 82.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 8 | ISO 179/1eA | ||
| -30°C | 3.0 | kJ/m² | |
| 23°C | 5.0 | kJ/m² | |
| Notched Izod Impact | |||
| 23°C, 6.40 mm | 49 | J/m | ASTM D256 |
| -30°C 9 | 4.0 | kJ/m² | ISO 180/1A |
| 23°C 10 | 5.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 11 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 105 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 87.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 110 | °C | ASTM D1525, ISO 306/B50 10 12 |
| -- | 112 | °C | ISO 306/B120 |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.2E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.4E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Constant | |||
| 1 MHz | 2.91 | ASTM D150 | |
| 1 MHz | 2.90 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 3.2E-3 | ASTM D150, IEC 60250 | |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-1 | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 725 | °C | |
| 2.00 mm | 725 | °C | |
| 3.00 mm | 725 | °C | |
| Oxygen Index | 34 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (280°C, 1500 sec^-1) | 95.0 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 50 to 70 | % | |
| Rear Temperature | 210 to 230 | °C | |
| Middle Temperature | 220 to 240 | °C | |
| Front Temperature | 230 to 250 | °C | |
| Nozzle Temperature | 220 to 240 | °C | |
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 60 | rpm | |
| Vent Depth | 0.038 to 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 sp=62mm |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M1685 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Matrixx TPP2B40 | The Matrixx Group, Inc. | PP Copolymer | Matrixx |
| SUMILITE® NS3450 | Sumitomo Bakelite Co., Ltd. | PP, Unspecified | SUMILITE® |
| SureSpec HW50-001 | Genesis Polymers | HDPE | SureSpec |
| ESTOPLAST ZK 6002NN02 | Ester Industries Ltd. | PC | ESTOPLAST ZK |