Santoprene™ 291-75B150 Datasheet,TPV,ExxonMobil Chemical-SHANGHAI SUSHENG

Message
It is a pigable special thermoplastic vulcanized elastomer (TPV) in the thermoplastic elastomer (TPE) series. It is specially formulated for bonding with PC, ABS, PC/ABS and PMMA, and is suitable for applications requiring a combination of hard/soft materials. This brand of Sanduping TPV is a shear rate dependent product that can be processed on conventional thermoplastic injection molding or extrusion molding equipment. Can be recycled online.

General Information
Features	Shock absorption Recyclable materials Adhesiveness Ozone resistance Good chemical resistance Oil resistance
Uses	Kitchen utensils Large household appliances and small household appliances Electrical appliances Active hinge Home appliance components Frame Seals Fatigue elimination supplies Parts under the hood of a car Application in Automobile Field Soft handle Mobile phone Sporting goods Consumer goods application field Bonding Bonding resin
Agency Ratings	UL QMFZ2 UL QMFZ8
RoHS Compliance	RoHS compliance
UL File Number	E80017
Appearance	Natural color
Forms	Particle
Processing Method	Multiple injection molding Co-extrusion molding Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.10	g/cm³	ASTM D792, ISO 1183

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shaw A, 15 seconds, 23°C, 2.00mm)	74		ISO 868

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress - Across Flow (100% Strain, 23°C)	3.20	MPa	ASTM D412, ISO 37
Tensile Strength - Across Flow (Break, 23°C)	15.4	MPa	ASTM D412, ISO 37
Tensile Elongation - Across Flow (Break, 23°C)	640	%	ASTM D412, ISO 37
Tear Strength - Across Flow
23°C ¹	46.0	kN/m	ASTM D624
23°C ²	46	kN/m	ISO 34-1
Compression Set
23°C, 22 hr ³	37	%	ASTM D395B
70°C, 22 hr ⁴	68	%	ASTM D395B
23°C, 22 hr ⁵	37	%	ISO 815
70°C, 22 hr ⁶	68	%	ISO 815

Aging	Nominal Value	Unit	Test Method
Change in Tensile Strength in Air (100°C, 168 hr)	-8.0	%	ASTM D573, ISO 188
Change in Ultimate Elongation in Air (100°C, 168 hr)	-11	%	ASTM D573, ISO 188
Change in Tensile Strength			ASTM D471, ISO 1817
23°C, 24 hr, in IRM 903 oil	-4.0	%	ASTM D471, ISO 1817
23°C, 168 hr, in 10% sodium hypochlorite	-16	%	ASTM D471, ISO 1817
23°C, 168 hr, in 10% hydrochloric acid	-19	%	ASTM D471, ISO 1817
23°C, 168 hr, in 15% sodium chloride	-18	%	ASTM D471, ISO 1817
23°C, 168 hr, in 50% sodium hydroxide	-16	%	ASTM D471, ISO 1817
23°C, 168 hr, in 50% ethanol	-71	%	ASTM D471, ISO 1817
23°C, 168 hr, at 90% relative temperature	-9.0	%	ASTM D471, ISO 1817
23°C, 168 hr, in series detergent	-16	%	ASTM D471, ISO 1817
38°C, 168 hr, at 90% relative temperature	-17	%	ASTM D471, ISO 1817
Change in Ultimate Elongation			ASTM D471, ISO 1817
23°C, 24 hr, in IRM 903 oil	1.0 -4.0	%	ASTM D471, ISO 1817
23°C, 168 hr, in 10% sodium hypochlorite	-1.0	%	ASTM D471, ISO 1817
23°C, 168 hr, in 10% hydrochloric acid	-1.0	%	ASTM D471, ISO 1817
23°C, 168 hr, in 15% sodium chloride	-2.0	%	ASTM D471, ISO 1817
23°C, 168 hr, in 50% sodium hydroxide	2.0	%	ASTM D471, ISO 1817
23°C, 168 hr, in 50% ethanol	-40	%	ASTM D471, ISO 1817
23°C, 168 hr, at 90% relative temperature	-7.0	%	ASTM D471, ISO 1817
23°C, 168 hr, in series detergent	3.0	%	ASTM D471, ISO 1817
38°C, 168 hr, at 90% relative temperature	-2.0	%	ASTM D471, ISO 1817
Change in Durometer Hardness (Support A, 23°C, 168 hr, in deionized water)	-2.0		ASTM D471, ISO 1817
Change in Mass			ASTM D471
23°C, 168 hr, in 10% sodium hypochlorite	0.50	%	ASTM D471
23°C, 168 hr, in 10% hydrochloric acid	0.50	%	ASTM D471
23°C, 168 hr, in 15% sodium chloride	0.50	%	ASTM D471
23°C, 168 hr, in 50% sodium hydroxide	0.10	%	ASTM D471
23°C, 168 hr, in 50% ethanol	8.6	%	ASTM D471
23°C, 168 hr, in 95% relative temperature	0.10	%	ASTM D471
23°C, 168 hr, in series detergent	0.50	%	ASTM D471
38°C, 168 hr, in 95% relative temperature	0.50	%	ASTM D471
Change in Mass			ISO 1817
23.0°C, 168 hr, in 95% relative temperature	0.10	%	ISO 1817
23.0°C, 168 hr, in 50% sodium hydroxide	0.10	%	ISO 1817
30.0°C, 168 hr, in 95% relative temperature	0.50	%	ISO 1817
23.0°C, 168 hr, in series detergent	0.50	%	ISO 1817
23.0°C, 168 hr, in 15% sodium chloride	0.50	%	ISO 1817
23.0°C, 168 hr, in 10% hydrochloric acid	0.50	%	ISO 1817
23.0°C, 168 hr, in 10% sodium hypochlorite	0.50	%	ISO 1817
23.0°C, 168 hr, in 50% ethanol	8.6	%	ISO 1817
Change in Volume
23°C, 168 hr, 95% relative humidity	0.10	%	ASTM D471
23°C, 168 hr, in 10% sodium hypochlorite	0.60	%	ASTM D471, ISO 1817
23°C, 168 hr, in 10% hydrochloric acid	0.60	%	ASTM D471
23°C, 168 hr, in 15% sodium chloride	0.60	%	ASTM D471
23°C, 168 hr, in 50% sodium hydroxide	0.20	%	ASTM D471
23°C, 168 hr, in 50% ethanol	9.3	%	ASTM D471, ISO 1817
23°C, 168 hr, in series detergent	0.60	%	ASTM D471, ISO 1817
38°C, 168 hr, 95% relative humidity	0.60	%	ASTM D471
23°C, 168 hr, in 10% hydrochloric acid	0.60	%	ISO 1817
23°C, 168 hr, in 15% sodium chloride	0.60	%	ISO 1817
23°C, 168 hr, in 50% sodium hydroxide	0.20	%	ISO 1817
23°C, 168 hr, at 95% relative humidity	0.10	%	ISO 1817
38°C, 168 hr, at 95% relative humidity	0.60	%	ISO 1817

Flammability	Nominal Value	Test Method
Flame Rating		UL 94
1.60 mm	HB	UL 94
2.10 mm	HB	UL 94

Additional Information
如果适用，这是基于扇形浇口注塑成型的平板测试结果。拉伸强度、伸长率和拉伸应力沿垂直流动方向测定 - ISO 1 型，ASTM die C。25% 形变时的永久压缩变形。从埃克森美孚欧洲分支机构直接购买的所有产品都符合 REACH 法规。对于埃克森美孚未进口至欧洲的产品，用户应自行评估其是否满足 REACH 法规。

Legal statement
未经埃克森美孚化工书面允许，这种产品包括其产品名称，不得在任何医疗应用领域予以使用或有关详细的产品监管信息，请联系客户服务。

Injection instructions
Santoprene TPV与乙缩醛和PVC不相容。更多信息请参见《291-XXB150快速加工参考手册》。

Note Message
1 .	C mould
2 .	Method B, right-angle specimen (cut)
3 .	Type 1
4 .	Type 1
5 .	Type a
6 .	Type a

Category:	TPV , Thermoplastic Vulcanizate
Manufacturer:	ExxonMobil Chemical
Trademark:	Santoprene™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	eYzNZU_Santoprene-291-75B150.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
VINIKA® CD50EA	Mitsubishi Chemical Performance Polymers, Inc.	PVC, Flexible	VINIKA®
LUVOCOM® 1105-8278/GY	Lehmann & Voss & Co.	PEEK	LUVOCOM®
Perfactory® ABflex	EnvisionTEC, Inc.	Acrylic, Unspecified	Perfactory®
Adstif HA600U	LyondellBasell Industries	PP Homopolymer	Adstif
PERLER® N09H1000A10	A.D. Compound S.p.A.	PP Copolymer	PERLER®