Lustran® SAN LK 273
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | INEOS ABS (USA) |
| Trademark: | Lustran® SAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eYVKPp_Lustran-SAN-LK-273.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lustran SAN LK 273 resin is an injection molding grade of transparent SAN (styrene acrylonitrile) thermoplastic. The base resin used in the Lustran SAN LK 273 product is in chemical compliance with 21 CFR 181.32 (acrylonitrile copolymers and resins) for use in the manufacture of repeated-use houseware articles. Lustran SAN LK 273 has a large molding window and is easy to process. The resin is available in crystal (552160) tint. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Specific Volume | 0.930 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 7.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 - 0.40 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 83 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3300 | MPa | ASTM D638 |
| Tensile Strength (Break) | 72.0 | MPa | ASTM D638 |
| Flexural Modulus | 3400 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 115 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 21 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, unannealed, 12.7mm | 96.0 | °C | ASTM D648 |
| 1.8 MPa, annealed, 12.7mm | 103 | °C | ASTM D648 |
| CLTE - Flow | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.570 | ASTM D542 | |
| Transmittance (3200 µm) | 87.0 - 88.0 | % | ASTM D1003 |
| Haze (3200 µm) | 0.70 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 82.0 - 88.0 | °C | |
| B | 71.0 - 77.0 | °C | |
| Drying Time | |||
| A | 2.0 | hr | |
| B | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Shot Size | 50 - 70 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 170 - 185 | °C | |
| Middle Temperature | 185 - 200 | °C | |
| Front Temperature | 200 - 215 | °C | |
| Nozzle Temperature | 200 - 215 | °C | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Pressure | 68.9 - 138 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.00 - 0.172 | MPa | |
| Clamp Tonnage | 2.8 - 5.5 | kN/cm² | |
| Cushion | 3.18 | mm | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Injection instructions |
|---|
| Screw Speed: ModerateInlet Air Dew Point: -20°FHold Pressure: 40 to 80% of the injection pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULINK® XL 350-S | A. Schulman Inc. | XLPE | SCHULINK® |
| DESLEN™ DSC501M6 | DESCO Co., Ltd. | PP, Unspecified | DESLEN™ |
| Edgetek™ PC-10CF/000 NH FR BK033 | PolyOne Corporation | PC | Edgetek™ |
| INEOS PP 101-CA06 | INEOS Olefins & Polymers Europe | PP Homopolymer | INEOS PP |
| PENTAMID A GK40 H schwarz | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |