ACRYLITE® H15 acrylic polymer is an amorphous thermoplastic molding and extrusion compound based on polymethyl methacrylate (PMMA).

Typical properties of ACRYLITE® acrylic polymers are:

excellent weather resistance

high light transmission

high mechanical strength

high surface hardness and mar resistance

good melt flow rate

versatile colorability due to crystal clarity

The special properties of ACRYLITE H15 polymer are:

medium heat resistance

high melt strength

UV light absorption options

lubricant options

AMECA listed

Application:
Used for injection molding and extrusion of optical and technical parts.

General Information
Features	Amorphous Good Colorability Good Flow Good Melt Strength Good Weather Resistance High Clarity High Hardness High Scratch Resistance High Strength Medium Heat Resistance UV Absorbing
Uses	Automotive Applications Decorative Displays Electrical/Electronic Applications Engineering Parts Lenses Lighting Applications Medical/Healthcare Applications Optical Applications Piping Profiles Rods Tubing
Agency Ratings	EC 1907/2006 (REACH)
Appearance	Clear/Transparent
Forms	Pellets
Processing Method	Extrusion Injection Molding Pipe Extrusion Profile Extrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.19	g/cm³	ASTM D792
Apparent Density	0.66	g/cm³	ASTM D1895
Melt Mass-Flow Rate (MFR) (230°C/3.8 kg)	2.2	g/10 min	ASTM D1238
Molding Shrinkage - Flow	0.40 to 0.70	%	ASTM D955
Water Absorption (Equilibrium)	< 0.30	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	95		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3240	MPa	ASTM D638
Tensile Strength	67.6	MPa	ASTM D638
Tensile Elongation			ASTM D638
Yield	4.0 to 6.0	%
Break	4.0 to 6.0	%
Flexural Modulus	3380	MPa	ASTM D790
Flexural Strength	117	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C, 6.35 mm)	19	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Annealed, 6.35 mm)	95.0	°C	ASTM D648
Vicat Softening Temperature	105	°C	ASTM D1525
CLTE - Flow (0 to 156°C)	7.2E-5	cm/cm/°C	ASTM D696

Optical	Nominal Value	Unit	Test Method
Transmittance (3200 µm)	92.0	%	ASTM D1003
Haze (3200 µm)	< 1.0	%	ASTM D1003
Yellowness Index (3.20 mm)	< 1.0	YI	ASTM D1925

Resin Grade	Manufacturer	Category	Trademark
RTP 301 TFE 5	RTP Company	PC	RTP
Vinnolit® K 707 E	Vinnolit GmbH & Co. KG	PVC Alloy	Vinnolit®
Hyundai EP PA6 LS260	HYUNDAI EP Co., Ltd.	Nylon 6	Hyundai EP PA6
Karina GREEN COLOR CONCENTRATE 40/447-FC	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
LNP™ LUBRICOMP™ FL004 compound	SABIC Innovative Plastics	PE, Unspecified	LNP™ LUBRICOMP™