TRANSMARE® 19HGF40-0.001
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Transmare Compounding B.V. |
| Trademark: | TRANSMARE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eXba0z_TRANSMARE-19HGF40-0-001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRANSMARE® 19HGF40-0.001 is a 40% glass fiber reinforced polypropylene homopolymer for injection molding purposes with very high stiffness and a good flow. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 4.5 | g/10 min | |
| 230°C/5.0 kg | 18 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 78 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, 4.00 mm) | 120 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 4.00 mm) | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 8750 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/A | ||
| -20°C | 8.5 | kJ/m² | |
| 0°C | 9.0 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -20°C | 10 | kJ/m² | |
| 0°C | 10 | kJ/m² | |
| 23°C | 13 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 156 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 144 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 161 | °C | ISO 306/A |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 203 D HS GB 20 TFE 15 | RTP Company | Nylon 612 | RTP |
| Tefzel® HT-2170 | DuPont Fluoropolymers | ETFE | Tefzel® |
| Flontech® FT-GL15-M3-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| K-Prene GHT 45 | Technovinyl Polymers India Ltd. | TPE | K-Prene |
| LOXIM 220 12 V0 | LOXIM Industries Private Limited | PBT | LOXIM |