ACCULOY™ PCS003L
| Category: | ASA+PC , Acrylonitrile Styrene Acrylate + PC |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCULOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eWSPLO_ACCULOY-PCS003L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCULOY™ PCS003L is an Acrylonitrile Styrene Acrylate + PC (ASA+PC) product. It is available in North America. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 62.0 | MPa | |
| Break | 52.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 6.0 | % | |
| Break | 100 | % | |
| Flexural Modulus | 2500 | MPa | ASTM D790 |
| Flexural Strength | 94.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 550 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 127 | °C | |
| 1.8 MPa, Unannealed | 106 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RJM SB302G30 | RJM International, Inc. | PBT | RJM |
| Spartech Polycom SCR7-7010R | Spartech Polycom | PC | Spartech |
| Geon™ Vinyl Flexible H43356A | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| KOPLA ABS KSG1010 | KOPLA Co., Ltd. | ABS | KOPLA ABS |
| LNP™ KONDUIT™ PX10323 compound | SABIC Innovative Plastics Europe | Nylon 6 | LNP™ KONDUIT™ |