CET® 116
| Category: | Acrylic (SMMA) , Styrene Methyl Methacrylate Acrylic Copolymer |
| Manufacturer: | Resirene, S.A. de C.V. |
| Trademark: | CET® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eVt2sq_CET-116.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A transparent styrene-acrylic copolymer with excellent clarity, good impact resistance, that is easy to process. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3280 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 52.1 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 3310 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 16 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 190 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 86.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 96.0 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 90.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Chemical Resistance 4 | ASTM D543 | ||
| Acetic Acid 20% : 25°C | Unaffected | ||
| Ethanol 50% : 25°C | Unaffected | ||
| Hand Soap 100% : 25°C | Unaffected |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 1.0 | hr | |
| Rear Temperature | 170 to 180 | °C | |
| Middle Temperature | 180 to 190 | °C | |
| Front Temperature | 200 to 210 | °C | |
| Nozzle Temperature | 210 to 220 | °C | |
| Processing (Melt) Temp | < 250 | °C | |
| Mold Temperature | 40.0 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 30 days |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starpylen MFK42AS | Eurostar Engineering Plastics | PP, Unspecified | Starpylen |
| NORYL™ GFN2F resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| IPC PP 4840C-T | International Polymers Corporation | PP Copolymer | IPC PP |
| LNP™ THERMOCOMP™ QF008 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ THERMOCOMP™ |
| LNP™ LUBRICOMP™ OCL36A compound | SABIC Innovative Plastics | PPS, Branched | LNP™ LUBRICOMP™ |