LNP™ THERMOCOMP™ EX11414 compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eVPHMS_LNP-THERMOCOMP-EX11414-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* THERMOCOMP* EX11414 is a compound based on Polyetherimide containing 20% Carbon Fiber. Also known as: LNP* THERMOCOMP* Compound EX11414 Product reorder name: EX11414 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr, 50% RH) | 0.23 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 17400 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 230 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 1.8 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 14600 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 50.0 mm Span) | 308 | MPa | ASTM D790 |
| Poisson's Ratio | 0.44 | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 78 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 600 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 213 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 - 1.0E+5 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 380 - 400 | °C | |
| Middle Temperature | 380 - 400 | °C | |
| Front Temperature | 380 - 400 | °C | |
| Processing (Melt) Temp | 380 - 400 | °C | |
| Mold Temperature | 165 - 180 | °C | |
| Back Pressure | 0.300 - 0.700 | MPa | |
| Screw Speed | 50 - 100 | rpm |
| Injection instructions |
|---|
| Injection Speed: 40 - 70 mm/s |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silamid® L | Roonamid a.s. | Nylon 6 | Silamid® |
| Andur M-22 (97% HQEE/ 3%TMP) | Anderson Development Company | PUR-Ester/MDI | Andur |
| Gallonprene® GP210-8009 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Electrafil® J-50/CF/10 | Techmer Engineered Solutions | PC | Electrafil® |
| INNOPOL® PP CS 1-2130 | Inno-Comp Ltd. | PP Homopolymer | INNOPOL® PP |