XYLEX™ X5230 resin
| Category: | PC+PET , Polycarbonate + PET |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | XYLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eVA5QG_XYLEXX5230resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Mineral filled PC/PET blend with high flow, high heat, dimensional stability, low shrinkage and low CTE, especially for painted applications |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.33 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (265°C/5.0 kg) | 28 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (265°C/5.0 kg) | 24.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.50 - 0.60 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.42 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.14 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3990 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 53.0 | MPa | ISO 527-2/5 |
| Fracture | 34.0 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 3.4 | % | ISO 527-2/5 |
| Fracture | 21 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 3820 | MPa | ISO 178 |
| Flexural Stress | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3(23°C) | 14 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact 4 | ISO 180/1A | ||
| -30°C | 6.0 | kJ/m² | ISO 180/1A |
| 23°C | 8.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 5 | ISO 180/1U | ||
| -30°C | 120 | kJ/m² | ISO 180/1U |
| 23°C | 140 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6(1.8 MPa, Unannealed, 64.0 mm Span) | 100 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 137 | °C | ISO 306/B50 |
| -- | 140 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : -30 to 80°C | 4.5E-5 | cm/cm/°C | ISO 11359-2 |
| Horizontal : -30 to 80°C | 9.7E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 120 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60 - 80 | °C | |
| Rear Temperature | 240 - 270 | °C | |
| Middle Temperature | 250 - 275 | °C | |
| Front Temperature | 260 - 280 | °C | |
| Nozzle Temperature | 260 - 275 | °C | |
| Processing (Melt) Temp | 265 - 275 | °C | |
| Mold Temperature | 60 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 218G2 V30 BLACK 34 N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Staramide A40 | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| DISTRUMID 6 GF30 HI | Distrupol | Nylon 6 | DISTRUMID |
| HAIPLEN H30 K6 BA X0 | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| Sylvin 8260-85UV Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |