SLOVAMID® 6 HI HV TS
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Plastcom |
| Trademark: | SLOVAMID® 6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eUuIWE_SLOVAMID-6-HI-HV-TS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6 is high viscosity, unreiforced, heat stabilised, impact modified for extrusion and blow moulding grade. Automotive aplications as air ducts and fuel filter pipes, fuel and oil containers. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/5.0 kg) | 10 | g/10 min | ISO 1133 |
| Water Content | 0.10 | % | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1900 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2 |
| Flexural Modulus | 750 | MPa | ISO 178 |
| Flexural Stress | 45.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 25 | kJ/m² | |
| 23°C | 85 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 44.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 175 | °C | ISO 306/B |
| Melting Temperature (DSC) | 222 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 475 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Viprene™ G55A-32U-BLK | Alliance Polymers & Services | TPV | Viprene™ |
| Nypol® PA A3 T40 PRTA011 NR321 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Grilamid® 2S 25 W 20 X black 9992 | EMS-GRIVORY | Nylon 610 | Grilamid® |
| Hipolyene 1535 T5 | Zylog Plastalloys | TPO (POE) | Hipolyene |
| Sylvin 2952-70 Brown 7466 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |