Durethan® BKV 30 H2.0 EF 901510
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eT2YC1_DurethanBKV30H20EF901510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 30 % glass fibers, injection molding, improved flowability, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.35 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.60 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 280°C, 2.00mm 1 | 0.81 | -- | % | ISO 294-4 |
| Vertical flow direction : 120°C, 2 hours, 2.00mm 2 | 0.10 | -- | % | ISO 294-4 |
| Flow direction : 280°C, 2.00mm 3 | 0.29 | -- | % | ISO 294-4 |
| Flow direction : 120°C, 2 hours, 2.00mm 4 | 0.050 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 7.0 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.1 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 193 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ||||
| 23°C | 8730 | -- | MPa | ASTM D638 |
| 23°C | 9400 | 5500 | MPa | ISO 527-2/1 |
| Tensile Strength | ||||
| Fracture, 23°C | 165 | -- | MPa | ASTM D638 |
| Fracture, 23°C | 170 | 100 | MPa | ISO 527-2/5 |
| Tensile Elongation | ||||
| Fracture, 23°C | 3.2 | -- | % | ASTM D638 |
| Fracture, 23°C | 3.0 | 5.8 | % | ISO 527-2/5 |
| Flexural Modulus | ||||
| 23°C | 8000 | -- | MPa | ASTM D790 |
| 23°C 5 | 8400 | 5000 | MPa | ISO 178/A |
| Flexural Strength | ||||
| 23°C | 260 | -- | MPa | ASTM D790 |
| 3.5% strain 6 | 255 | 140 | MPa | ISO 178/A |
| 23°C 7 | 260 | 170 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 8(23°C) | 3.6 | 5.5 | % |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behavior 9 | passed | -- | ISO 3795 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GHR, 10-090, GF30 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Films | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Film Puncture Energy | ISO 6603-2 | |||
| -- 10 | 2.10 | -- | J | ISO 6603-2 |
| -- 11 | 2.20 | -- | J | ISO 6603-2 |
| Film Puncture Force | ISO 6603-2 | |||
| -- 12 | 744 | -- | N | ISO 6603-2 |
| -- 13 | 803 | -- | N | ISO 6603-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | < 10 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 11 | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 55 | 55 | kJ/m² | ISO 179/1eU |
| 23°C | 65 | 80 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | < 10 | -- | kJ/m² | ISO 180/1A |
| 23°C | 10 | 20 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 55 | 50 | kJ/m² | ISO 180/1U |
| 23°C | 60 | 75 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 219 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 210 | -- | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 150 | -- | °C | ISO 75-2/C |
| Vicat Softening Temperature | 210 | -- | °C | ISO 306/B120 |
| Ball Pressure Test (210°C) | Pass | -- | IEC 60695-10-2 | |
| Melting Temperature 14 | 221 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 2.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 1.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Dielectric Strength (23°C, 1.00 mm) | 33 | 25 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (Solution A) | 400 | -- | V | IEC 60112 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 250 - 290 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; MT 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; MT 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | Pull Rate: 2 mm/min; 50% RH |
| 9 . | US-FMVSS302 |
| 10 . | -30°C |
| 11 . | 23°C |
| 12 . | -30°C |
| 13 . | 23°C |
| 14 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYSTONE® P copolymer | Röchling Engineering Plastics SE & Co. KG | PP Copolymer | POLYSTONE® |
| Geon™ Vinyl Wire & Cable WJAX208U | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Wire & Cable |
| Latimass 66-04 D009 | LATI S.p.A. | Nylon 66 | Latimass |
| Paracril OZO® M50 | INSA | PVC+NBR | Paracril OZO® |
| Petrothene® LP510031 | LyondellBasell Industries | HDPE | Petrothene® |