SABIC® STAMAX 30YM243
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® STAMAX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eSetoO_SABIC-STAMAX-30YM243.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC® STAMAX 30YM243 is a 30% long glass fiber reinforced UV stabilised grade. The glass fibres are chemically coupled to the PP matrix, resulting in high stiffness and strength. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1B | ||
| 23°C, Injection Molded | 6650 | MPa | |
| 80°C, Injection Molded | 4600 | MPa | |
| 120°C, Injection Molded | 3500 | MPa | |
| Tensile Stress 1 | ISO 527-2 | ||
| 23°C, Injection Molded | 110 | MPa | |
| 80°C, Injection Molded | 70.0 | MPa | |
| 120°C, Injection Molded | 51.0 | MPa | |
| Tensile Strain (Break, 23°C, Injection Molded) | 2.3 | % | ISO 527-2/1B |
| Flexural Modulus | ISO 178 | ||
| 23°C, Injection Molded | 5900 | MPa | |
| 80°C, Injection Molded | 4200 | MPa | |
| Flexural Stress | ISO 178 | ||
| 23°C, Injection Molded | 147 | MPa | |
| 80°C, Injection Molded | 86.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C, Injection Molded | 25 | kJ/m² | |
| 23°C, Injection Molded | 19 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C, Injection Molded | 36 | kJ/m² | |
| 23°C, Injection Molded | 52 | kJ/m² | |
| Falling Dart Impact - Total Energy 2(23°C) | 58.0 | J/cm | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 156 | °C | ISO 75-2/A |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 5.1E-5 | cm/cm/°C | |
| 23 to 80°C | 4.1E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Type 1B |
| 2 . | Injection Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VERSIFY™ 2200 | The Dow Chemical Company | POP | VERSIFY™ |
| Celstran® +PP-GF40-04CN03/10 | Celanese Corporation | PP, Unspecified | Celstran® |
| ESTAPROP H 0360 T8 | Cossa Polimeri S.r.l. | PP Homopolymer | ESTAPROP |
| Karina IVORY PVC COMPOUND KAPU 6535/1-Y (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plexar® PX5335 | LyondellBasell Industries | LLDPE | Plexar® |