ICORENE® 1506 BLACK 9001
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | A. Schulman Europe |
| Trademark: | ICORENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eRUNuW_ICORENE1506BLACK9001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ICORENE® 1506 BLACK 9001 is a crosslinkable high density polyethylene specifically developed for rotational moulding. ICORENE® 1506 BLACK 9001 is particularly suitable for use in applications requiring exceptional impact resistance at low temperature, toughness and excellent ESCR such as fuel tanks. The cross linking system used allows a wider processing windows and higher PIAT can be reached. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Environmental Stress-Cracking Resistance 1(50°C) | > 1000 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 20.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 600 | % | ASTM D638 |
| Flexural Modulus | 750 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drop Impact Resistance (-40°C) | 320 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 43.0 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 10% IGEPAL |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Verolloy B2703 | PlastxWorld Inc. | ABS+PBT | Verolloy |
| Biograde B-F | Biograde Group of Companies | Biodeg Polymers | Biograde |
| AT 191A | Celanese EVA Performance Polymers | LDPE | AT |
| Fainplast PVC PH 60/A | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Infino GM-1080 | LOTTE ADVANCED MATERIALS CO., LTD. | PC | Infino |