Aristech Solarcast®
| Category: | Acrylic, Unspecified , Acrylic |
| Manufacturer: | Aristech Acrylics LLC |
| Trademark: | Aristech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eQlcyR_Aristech-Solarcast-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Aristech Acrylics LLC Solarcast® Acrylic Sheet is an "ultraviolet transmitting" cast acrylic sheet derived from a unique formulation. Aristech Acrylics LLC Solarcast® Acrylic Sheet was developed particularly for tanning bed and other applications where UV transmittance is needed. The following physical properties were determined using 0.177" (4.5 mm) thickness clear Aristech Acrylics LLC Acrylic Sheet. Properties may vary somewhat on other thicknesses. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.18 | g/cm³ | ASTM D792 |
| Water Absorption (Saturation, 4.50 mm) | 0.18 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale, 4.50 mm) | 101 | ASTM D785 | |
| Barcol Hardness (4.50 mm) | 54 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (4.50 mm) | 3250 | MPa | ASTM D638 |
| Tensile Strength (Yield, 4.32 mm) | 64.6 | MPa | ASTM D638 |
| Tensile Elongation (Break, 4.50 mm) | 3.3 | % | ASTM D638 |
| Flexural Modulus (4.50 mm) | 3170 | MPa | ASTM D790 |
| Flexural Strength (4.50 mm) | 120 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (4.50 mm) | 315 | J/m | ASTM D6110 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Stability (180°C, 4.50 mm) 2 | No degradation | ASTM D4802 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| UV Transmittance 3 | |||
| 280 nm | 63 | % | |
| 300 nm | 82 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Forming Temperature (4.50 mm) | 171 to 193 | °C | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (4.50 mm) | 22 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 4.50 mm) | 95.6 | °C | ASTM D648 |
| CLTE - Flow (4.50 mm) | 6.5E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat 4 | 1460 | J/kg/°C | ASTM C351 |
| Thermal Conductivity 5 | 0.20 | W/m/K | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 6 | 1.490 | ASTM D542 | |
| Transmittance (4500 µm) | 92.6 | % | ASTM D1003 |
| Haze (4500 µm) | 1.5 | % | ASTM D1003 |
| Yellowness Index (4.50 mm) | 0.70 | YI | ASTM D1925 |
| Note Message | |
|---|---|
| 1 . | 0.177 in |
| 2 . | 30 min |
| 3 . | UV Spectrophotometer |
| 4 . | 0.177 in |
| 5 . | 0.177 in |
| 6 . | 0.177 in |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYshine PBT D221 | Polykemi AB | PBT | POLYshine |
| Topolymer® 5211-851E | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| Chemical Resources RPP 100CW | Chemical Resources, Inc. | PP Random Copolymer | Chemical Resources |
| HiFill® PA6/6 GF/M35 HS BK | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Sylvin 8376-92UV Black 298 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |