Order Products : sales@su-jiao.com
STARFLEX® P 7393-1000
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | STAR Thermoplastic Alloys & Rubbers, Inc. |
| Trademark: | STARFLEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eQ4nqA_STARFLEX-P-7393-1000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| STARFLEX® P 7393-1000 is a Thermoplastic Elastomer (TPE) material. It is available in North America for extrusion or injection molding. Primary attribute of STARFLEX® P 7393-1000: Good Weather Resistance. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.0 to 1.5 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 93 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (300% Strain) | 8.76 | MPa | ASTM D412 |
| Tensile Strength (Break) | 8.96 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 330 | % | ASTM D412 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 182 to 193 | °C | |
| Front Temperature | 188 to 199 | °C | |
| Nozzle Temperature | 199 to 210 | °C | |
| Mold Temperature | 37.8 to 60.0 | °C | |
| Injection Pressure | 3.45 to 4.83 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.552 to 1.03 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RMA 160 | Ronald Mark Associates, Inc. | PVC Homopolymer | RMA |
| NaturePlast PBE 003 | NaturePlast | Polyester, TP | NaturePlast |
| Nymax™ GMF 600 A 40 Natural | PolyOne Corporation | Nylon 6 | Nymax™ |
| Polimid A 35 GF V0F K | Poliblend S.p.a. | Nylon 66 | Polimid A |
| Sylvin 9776-95 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |