Grilamid® TR 30 nat
| Category: | Nylon 6I/X , Polyamide 6I/X Copolymer |
| Manufacturer: | EMS-GRIVORY |
| Trademark: | Grilamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ePodOz_Grilamid-TR-30-nat.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Grilamid® TR 30 nat is a Polyamide 6I/X Copolymer (Nylon 6I/X) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for calendering, injection molding, or injection stretch blow molding. Primary attribute of Grilamid® TR 30 nat: Flame Rated. Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.15 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.70 | -- | % | |
| Flow | 0.70 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 7.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | -- | 160 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | -- | 2800 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | -- | 90.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | |||
| Yield | -- | 6.0 | % | |
| Break | -- | > 50 | % |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | -- | 12 | kJ/m² | |
| 23°C | -- | 12 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | -- | No Break | ||
| 23°C | -- | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 135 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 125 | -- | °C | ISO 75-2/A |
| Maximum Use Temperature | Internal Method | |||
| Long Term | 80 to 100 | -- | °C | |
| Short Term | 120 | -- | °C |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Type | PA 6I/X , GT, 12-030 | -- | ISO 1874 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Glass Transition Temperature 1 | 160 | -- | °C | ISO 11357-2 |
| CLTE | ISO 11359-2 | |||
| Flow | 6.0E-5 | -- | cm/cm/°C | |
| Transverse | 6.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | -- | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | -- | 27 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification (0.800 mm) | V-2 | -- | IEC 60695-11-10, -20 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PREMIER™ A230-FRHF | Chomerics, div. of Parker Hannifin Corp. | PC+ABS | PREMIER™ |
| megol® PUG 60 | API SpA | SEBS | megol® |
| Nycal™ 2150R33F1 | Technical Polymers, LLC | Nylon 66 | Nycal™ |
| Bergamid™ B700 G25 H | PolyOne Corporation | Nylon 6 | Bergamid™ |
| Crastin® SK642FR NC010 | DuPont Performance Polymers | PBT | Crastin® |