Lupolen 3020 H PLUS
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Lupolen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ePa4BF_Lupolen-3020-H-PLUS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lupolen 3020 H PLUS is a non-additivated, low density polyethylene with high rigidity, good opticals and good chemical resistance. This grade is characterized by a very low gel level. Typical customer applications are lamination films or other higher value film applications where a very low gel content is required . It is delivered in pellet form. Foodlaw compliance information about this product can be found in separate product documentation. This product is not intended for use in medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.928 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 300 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 13.0 | MPa | ISO 527-2 |
| Coefficient of Friction (Blown Film) | > 0.80 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Film Thickness - Recommended / Available | 20-60 um | ||
| Tensile Strength | ISO 527-3 | ||
| MD : 50 µm, blown film | 25.0 | MPa | ISO 527-3 |
| TD : 50 µm, blown film | 20.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 350 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 600 | % | ISO 527-3 |
| Dart Drop Impact (50 µm, Blown Film) | 110 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 100 | °C | ISO 306/A50 |
| Melting Temperature (DSC) | 114 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 20, 50.0 µm, blown film | > 70 | ASTM D2457 | |
| 60, 50.0 µm, blown film | > 110 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | < 6.5 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Failure Energy (50.0 µm) | 40.0 | J/cm | DIN 53373 |
| Film property tested using 50 µm thickness blown film extruded at a melt temperature of 180°C and a blow-up ratio of 1:2.5. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 200 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Safrene® M 5010SH | Safripol (PTY) LTD | HDPE | Safrene® |
| SCHULAFORM® 9 A GF 25 | A. Schulman Europe | Acetal (POM) Copolymer | SCHULAFORM® |
| SUNPRENE® FF55JC | Mitsubishi Chemical Performance Polymers, Inc. | PVC Elastomer | SUNPRENE® |
| LEXAN™ 103 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| CALIBRE™ 351-6 | Sumika Styron Polycarbonate Limited | PC | CALIBRE™ |