PrimePart® PLUS PA 2221
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | EOS GmbH |
| Trademark: | PrimePart® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eP1nni_PrimePart-PLUS-PA-2221.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PrimePart® PLUS (PA 2221) is a refresh optimised polyamide 12 powder for processing in laser sintering systems. Therefore the need for new powder is considerably reduced, making PrimePart® PLUS economically very attractive. Laser sintered parts from PrimePart® PLUS are natural coloured and a little translucent. Properties
Acceptance criteria
Typical applications
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.970 | g/cm³ | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 75 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1650 | MPa | ISO 527-2 |
| -- 2 | 1600 | MPa | ISO 527-2 |
| Tensile Stress | |||
| -- 3 | 40.0 | MPa | ISO 527-2 |
| -- 4 | 47.0 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Break 5 | 16 | % | ISO 527-2 |
| Break 6 | 4.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C 7 | 1390 | MPa | ISO 178 |
| 23°C 8 | 1340 | MPa | ISO 178 |
| Flexural Stress | |||
| 8.4% Strain 9 | 59.0 | MPa | ISO 178 |
| 8.2% Strain 10 | 54.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23°C 11 | 3.2 | kJ/m² | ISO 179/1eA |
| 23°C 12 | 3.9 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | |||
| 23°C 13 | 18 | kJ/m² | ISO 179/1eU |
| 23°C 14 | 35 | kJ/m² | ISO 179/1eU |
| 23°C 15 | 61 | kJ/m² | ISO 179/1fU |
| 23°C 16 | 22 | kJ/m² | ISO 179/1fU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed 17 | 157 | °C | ISO 75-2/B |
| 0.45 MPa, Unannealed 18 | 148 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed 19 | 69.0 | °C | ISO 75-2/A |
| 1.8 MPa, Unannealed 20 | 70.0 | °C | ISO 75-2/A |
| Melting Temperature 21 | 187 | °C | ISO 11357 |
| Note Message | |
|---|---|
| 1 . | X Direction |
| 2 . | Z Direction |
| 3 . | Z Direction |
| 4 . | Y Direction |
| 5 . | X Direction |
| 6 . | Z Direction |
| 7 . | X Direction |
| 8 . | Z Direction |
| 9 . | X Direction |
| 10 . | Z Direction |
| 11 . | Z Direction |
| 12 . | Y Direction |
| 13 . | Z Direction |
| 14 . | Y Direction |
| 15 . | X Direction |
| 16 . | Z Direction |
| 17 . | X Direction |
| 18 . | Z Direction |
| 19 . | Z Direction |
| 20 . | Y Direction |
| 21 . | 20°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT7016-01UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| TechnoMid A200 FL | TechnoCompound GmbH | Nylon 66 | TechnoMid |
| Tenac™-C 8520 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| Telcar® GS6073 | Teknor Apex Asia Pacific PTE. LTD. | TPE | Telcar® |
| Sylvin 8904-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |