PENTESTER ET GV30 H schwarz
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTESTER ET |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eOLGZH_PENTESTER-ET-GV30-H-schwarz.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Normal viscosity, heat stabilised polyester PET, 30% glass fiber reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.56 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.80 | % | ISO 294-4 |
| Flow direction | 0.40 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.50 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.18 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 235 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11400 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 155 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.1 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 245 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 225 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 255 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (1.00 mm) | 32 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.90 | IEC 60250 | |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 |
| Additional Information |
|---|
| ISO Description: PET, MPRMC, 13-110; GF30The value listed as Melting Point, ISO 3146, was tested in accordance with ISO 11357. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.014 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 265 - 290 | °C | |
| Middle Temperature | 280 - 295 | °C | |
| Front Temperature | 280 - 290 | °C | |
| Processing (Melt) Temp | 285 | °C | |
| Mold Temperature | 130 | °C | |
| Injection Pressure | 78.0 | MPa | |
| Holding Pressure | 46.8 | MPa | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Cosmic DAP D62/6130F | Cosmic Plastics, Inc. | DAP | Cosmic DAP |
| Kingfa HG-105 | Kingfa | PP, Unspecified | Kingfa |
| Hostacom SP 98/F | LyondellBasell Industries | PP Copolymer | Hostacom |
| PLUSTEK PB340S6 | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |
| POFEX EP8300S 90M | POLYROCKS CHEMICAL CO., LTD | TPU, Unspecified | POFEX |