| PBT, non-reinforced, extrusion, food contact |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.30 | g/cm³ | ISO 1183 |
| Apparent Density | 0.80 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Across Flow : 260°C, 3.00 mm 1 | 1.6 | % | |
| Across Flow : 150°C, 1 hr, 3.00 mm 2 | 0.50 | % | |
| Flow : 260°C, 3.00 mm 3 | 1.6 | % | |
| Flow : 150°C, 1 hr, 3.00 mm 4 | 0.50 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.50 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % | |
| Viscosity Number (Reduced Viscosity) | 158.0 | ml/g | ISO 1628 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2600 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 55.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 4.0 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | > 50 | % | ISO 527-2/50 |
| Flexural Stress | ISO 178/A | ||
| 3.5% Strain, 23°C | 75.0 | MPa | |
| 23°C 5 | 85.0 | MPa | |
| Flexural Strain at Flexural Strength 6(23°C) | 6.0 | % | ISO 178/A |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PBT, G, 13-030 | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 to 0.020 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | < 10 | kJ/m² | |
| 23°C | < 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 230 | kJ/m² | |
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | < 10 | kJ/m² | |
| 23°C | < 10 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 180 | kJ/m² | |
| 23°C | No Break | ||
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | ||
| -30°C | 16.0 | J | |
| 23°C | 23.0 | J | |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | ||
| -30°C | 3930 | N | |
| 23°C | 3880 | N |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 140 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 60.0 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 45.0 | °C | ISO 75-2/C |
| Vicat Softening Temperature | 170 | °C | ISO 306/B120 |
| Melting Temperature 7 | 225 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 1.3E-4 | cm/cm/°C | |
| Transverse : 23 to 55°C | 1.3E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.40 | ||
| 23°C, 1 MHz | 3.20 | ||
| Dissipation Factor | IEC 60250 | ||
| 23°C, 100 Hz | 1.5E-3 | ||
| 23°C, 1 MHz | 0.020 | ||
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.60 mm | HB |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Circulation Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 to 8.0 | hr |
| Note Message | |
|---|---|
| 1 . | 150x105x3mm, 80°C MT, 600 bar |
| 2 . | 150x105x3mm |
| 3 . | 150x105x3mm, 80°C MT, 600 bar |
| 4 . | 150x105x3mm |
| 5 . | 2.0 mm/min |
| 6 . | 2 mm/min |
| 7 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Tech™ AS-1000 AS | PolyOne Corporation | ABS | Stat-Tech™ |
| Wellamid® MRGF25/15 42H-NBK1R | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| COSMOPLENE® FL7016G | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP Homopolymer | COSMOPLENE® |
| Geon™ Vinyl Flexible XV3875 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Honeywell PCTFE P2000TR | Honeywell | PCTFE | Honeywell PCTFE |