BT200 is a natural, 20% mineral filled polypropylene compound intended for injection moulding and extrusion profile. BT200 has a rather low flow rate and outstanding process ability. APPLICATIONS
Products requiring excellent rigidity, low shrinkage and high dimensional stability can suitably be made from BT200. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.1 - 1.6 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2550 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 31.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 8.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2490 | MPa | ISO 178 |
| Flexural Stress 2 | 42.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 70 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 122 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 70.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 154 | °C | ISO 306/A |
| Ball Pressure Test (125°C) | Pass | NF C 61-303 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 210 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miramid® VEP15C | BASF Leuna GmbH | Nylon 6 | Miramid® |
| Stat-Tech™ ATC-000/000 AS Natural | PolyOne Corporation | Acetal (POM) Copolymer | Stat-Tech™ |
| ExTima™ GP MB PA66 630 | Ovation Polymers Inc. | Nylon 66 | ExTima™ |
| ELASTOSIL® R 701/70 | Wacker Chemie AG | Silicone | ELASTOSIL® R |
| UNITIKA Nylon 6 M2350 | UNITIKA Plastics Division | Nylon 6 | UNITIKA Nylon 6 |