Amodel AFA- 6133 V0 Z is a 33% glass fiber reinforced flame retardant polyphthalamide (PPA) resin, specially developed for connectors commonly used in the electronic industry that can adapt to infrared and vapor welding. Amodel AFA-6133 V0 Z has high fluidity and short molding cycle, so it can improve molding efficiency and reduce costs. -black: AFA-6133 V0 Z BK 324

General Information
Filler / Reinforcement	Glass fiber reinforced material, 33% filler by weight
Additive	Flame retardancy
Features	Good dimensional stability Rigid, good High strength Good electrical performance High liquidity Good chemical resistance Hot water formability Flame retardancy
Uses	Electrical/Electronic Applications Connector Automotive Electronics Application in Automobile Field spool
RoHS Compliance	RoHS compliance
Appearance	Black
Forms	Particle
Processing Method	Water temperature mold injection molding
Multi-Point Data	Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)
Part Marking Code (ISO 11469)	>PA6T/66-GF33
Resin ID (ISO 1043)	PA6T/66 GF33 FR(17)

Physical	Dry	Conditioned	Unit	Test Method
Density	1.68	--	g/cm³	ISO 1183/A
Molding Shrinkage				ASTM D955
Flow	0.30	--	%	ASTM D955
Transverse flow	0.60	--	%	ASTM D955
Water Absorption (24 hr)	0.20	--	%	ASTM D570

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus
--	16100	13700	MPa	ASTM D638
23°C	14500	14500	MPa	ISO 527-2
100°C	9170	9200	MPa	ISO 527-2
150°C	5930	5900	MPa	ISO 527-2
175°C	5100	5100	MPa	ISO 527-2
Tensile Stress
Yield, 23°C	186	186	MPa	ISO 527-2
Yield, 100°C	114	114	MPa	ISO 527-2
Yield, 150°C	75.2	75.2	MPa	ISO 527-2
Yield, 175°C	63.4	63.4	MPa	ISO 527-2
--	199	166	MPa	ASTM D638
Tensile Elongation
Fracture	1.7	1.7	%	ASTM D638
Fracture, 23°C	1.6	1.6	%	ISO 527-2
Fracture, 100°C	2.4	2.4	%	ISO 527-2
Fracture, 150°C	5.1	5.1	%	ISO 527-2
Fracture, 175°C	4.9	4.9	%	ISO 527-2
Flexural Modulus
--	13100	13300	MPa	ASTM D790
23°C	12600	12600	MPa	ISO 178
100°C	8070	8100	MPa	ISO 178
150°C	4960	5000	MPa	ISO 178
175°C	4620	4600	MPa	ISO 178
Flexural Strength
--	224	229	MPa	ASTM D790
23°C	259	259	MPa	ISO 178
100°C	161	161	MPa	ISO 178
150°C	101	101	MPa	ISO 178
175°C	87.6	88.0	MPa	ISO 178
Compressive Strength	145	--	MPa	ASTM D695
Shear Strength	80.0	62.1	MPa	ASTM D732

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength
23°C	14	--	kJ/m²	ISO 179/1eA
23°C	--	14	kJ/m²	ISO 179/2eA
Charpy Unnotched Impact Strength (23°C)	46	47	kJ/m²	ISO 179/1eU
Notched Izod Impact
--	85	80	J/m	ASTM D256
23°C	8.2	8.0	kJ/m²	ISO 180/1A
Unnotched Izod Impact
--	690	--	J/m	ASTM D256
23°C	44	44	kJ/m²	ISO 180/1U

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
1.8 MPa, not annealed	282	282	°C	ISO 75-2/Af
1.8 MPa, annealed	277	--	°C	ASTM D648
Melting Temperature
--	310	310	°C	ISO 11357-3
--	310	--	°C	ASTM D3418
Linear thermal expansion coefficient				ASTM E831
Flow : 0 to 100°C	1.7E-5	--	cm/cm/°C	ASTM E831
Flow : 100 to 200°C	7.0E-6	--	cm/cm/°C	ASTM E831
Lateral : 0 to 100°C	6.4E-5	--	cm/cm/°C	ASTM E831
Lateral : 100 to 200°C	1.1E-4	--	cm/cm/°C	ASTM E831

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	1.0E+15	--	ohms	ASTM D257
Volume Resistivity	1.0E+15	--	ohms·cm	ASTM D257
Dielectric Strength (3.18 mm)	24	--	kV/mm	ASTM D149
Dielectric Constant				ASTM D150
100 Hz	4.40	--		ASTM D150
1 MHz	4.10	--		ASTM D150
Dissipation Factor (1 MHz)	0.011	--		ASTM D150
Comparative Tracking Index (CTI)	PLC 1	--		UL 746
High Amp Arc Ignition (HAI)				UL 746
0.749 mm	PLC 0	--		UL 746
1.50 mm	PLC 0	--		UL 746
3.00 mm	PLC 0	--		UL 746
Hot-wire Ignition (HWI)				UL 746
0.749 mm	PLC 0	--		UL 746
1.50 mm	PLC 0	--		UL 746
3.00 mm	PLC 0	--		UL 746

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating ¹(0.800 mm)	V-0	--		UL 94

Injection instructions
射出速度： 3〜4英寸/秒保压压力：射出压力的50%

Note Message
1 .	These flammability ratings do not represent the risk of these materials or any other materials in actual fire situations.

Category:	PPA , Polyphthalamide
Manufacturer:	Solvay Specialty Polymers
Trademark:	Amodel®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	eNQPGa_Amodel-AFA-6133-V0-Z.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
ECO-FLEX鈩?SA-40D	SYNESIS LLC	RTPV	Ecoflex® Supersoft
Hanwha Total PE E180F	HANWHA TOTAL PETROCHEMICALS Co., Ltd.	EVA	Hanwha Total PE
KEBAFLEX® E 80.1	BARLOG plastics GmbH	TPV	KEBAFLEX®
LUBMER™ L4640	Mitsui Chemicals, Inc.	HMWPE	LUBMER™
Sylvin 5132-86 Clear White 1448	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin