LEXAN™ LUX2110T resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eKZ7cY_LEXAN-LUX2110T-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Global grade. LEXAN LUX2110T is an injection molding grade especially designed for manufacturing optical parts requiring easy flow properties combined with very high transmission and color stability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 19 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow 1 | 0.60 to 0.90 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 2 | 2220 | MPa | ASTM D638 |
| Tensile Strength 3 | ASTM D638 | ||
| Yield | 60.0 | MPa | |
| Break | 68.0 | MPa | |
| Tensile Elongation 4 | ASTM D638 | ||
| Yield | 7.0 | % | |
| Break | 140 | % | |
| Flexural Modulus 5(50.0 mm Span) | 2360 | MPa | ASTM D790 |
| Flexural Strength 6(Yield, 50.0 mm Span) | 96.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 140 | J/m | |
| 23°C | 790 | J/m | |
| Unnotched Izod Impact (23°C) | 2100 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 72.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 142 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 129 | °C | |
| Vicat Softening Temperature | 145 | °C | ISO 306/B120 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 95°C | 6.5E-5 | cm/cm/°C | |
| Transverse : -40 to 95°C | 6.4E-5 | cm/cm/°C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2540 µm) | > 90.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 271 to 293 | °C | |
| Middle Temperature | 282 to 304 | °C | |
| Front Temperature | 293 to 316 | °C | |
| Nozzle Temperature | 288 to 310 | °C | |
| Processing (Melt) Temp | 293 to 316 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Milastomer™ 8032NS | Mitsui Chemicals America, Inc. | TPV | Milastomer™ |
| Westlake LDPE EC800AA | Westlake Chemical Corporation | LDPE | Westlake LDPE |
| AKROMID® B3 GF 35 1 black (2486) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| FORMULA P ELAN 5220 M2 Z | Putsch Kunststoffe GmbH | PP, Unspecified | FORMULA P |
| Karina IVORY PVC COMP. -E 850-35/ 1-G-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |