3M™ Dyneon™ Fluoroelastomer FE 5522

Category:	Fluorelastomer , Fluoroelastomer
Manufacturer:	3M Advanced Materials Division
Trademark:	3M™ Dyneon™ Fluoroelastomer
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	eIaioq_3MDyneonFluoroelastomerFE5522.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
3M™ Dyneon™ Fluoroelastomer FE 5522 is a terpolymer made from hexafluoropropylene, vinylidene fluoride and tetrafluoroethylene. It is a raw gum without curatives. Special Features Composition: Low fluorine content terpolymer of vinylidene fluoride, hexyfluoropropylene, and tetrafluoroethylene Process targets: Injection and transfer moulding Improved low temperature flexibility over standard dipolymers and terpolymers Medium viscosity gum stock without incorporated curatives Amine and bisphenol curable Typical Applications 3M™ Dyneon™ Fluoroelastomer FE 5522 is a medium viscosity raw gum to be used to adjust parameters, e.g. crosslink density and viscosity.

Message

3M™ Dyneon™ Fluoroelastomer FE 5522 is a terpolymer made from hexafluoropropylene, vinylidene fluoride and tetrafluoroethylene. It is a raw gum without curatives.

Special Features

Composition: Low fluorine content terpolymer of vinylidene fluoride, hexyfluoropropylene, and tetrafluoroethylene

Process targets: Injection and transfer moulding

Improved low temperature flexibility over standard dipolymers and terpolymers

Medium viscosity gum stock without incorporated curatives

Amine and bisphenol curable

Typical Applications
3M™ Dyneon™ Fluoroelastomer FE 5522 is a medium viscosity raw gum to be used to adjust parameters, e.g. crosslink density and viscosity.

General Information
Features	Terpolymer Medium viscosity
Uses	Plastic modification
Forms	Thick sheet
Processing Method	Resin transfer molding Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.80	g/cm³	Internal method
Mooney Viscosity (ML 1+10, 121°C)	29	MU	Internal method
Fluorine Content	66	%	Internal method

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	75		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress ¹(100% Strain)	6.50	MPa	ASTM D412A
Tensile Strength ²	13.8	MPa	ASTM D412A
Tensile Elongation ³(Break)	180	%	ASTM D412A
Compression Set (200°C, 70 hr)	20	%	ASTM D1414

Note Message
1 .	D mould
2 .	Die D
3 .	D mould

Resin Grade	Manufacturer	Category	Trademark
SABIC® PPcompound 9152	Saudi Basic Industries Corporation (SABIC)	PP, Unspecified	SABIC® PPcompound
TIPPLEN® K 597	MOL Petrochemicals Co. Ltd.	PP Impact Copolymer	TIPPLEN®
NYCOA Polyamide 2025	Nycoa (Nylon Corporation of America)	Nylon 6	NYCOA Polyamide
Kumho SBR 1500NF	Korea Kumho Petrochemical Co., Ltd.	SBR, Emulsion	Kumho SBR
Sylvin 8480-85 Natural	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin