DOWLEX™ IP 10
| Category: | HDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eIaFL6_DOWLEX-IP-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
DOWLEX™ IP 10 Polyethylene Resin is an Improved Processing high density resin specifically designed for reusable case applications including: poultry, fast food, automotive, retail, fresh produce, beverages, food service and chemicals, including plastics. Excellent processability is achieved with this resin due to its easy flow at low temperatures. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.960 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 100% Igepal, F50) | 8.00 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 55 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 29.0 | MPa | ASTM D638 |
| Fracture | 18.6 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 7.0 | % | ASTM D638 |
| Fracture | 1200 | % | ASTM D638 |
| Flexural Modulus - 2% Secant | 1160 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength 1 | 105 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 81.1 | °C | ASTM D648 |
| Brittleness Temperature | < -101 | °C | ASTM D746 |
| Vicat Softening Temperature | 130 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 132 | °C | Internal method |
| Peak Crystallization Temperature (DSC) | 119 | °C | Internal method |
| Additional Information |
|---|
| 根据 ASTM D 4976 进行基板模制和测试。 |
| Note Message | |
|---|---|
| 1 . | Type s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAC® PA-764B | CHI MEI CORPORATION | ABS | POLYLAC® |
| Starpylen MZ006S | Eurostar Engineering Plastics | PP, Unspecified | Starpylen |
| NaturePlast PLE 001 | NaturePlast | PLA | NaturePlast |
| NILAMID® B3 TM2 | Nilit Plastics | Nylon 6 | NILAMID® |
| AKROTEK® PK-VM GF 15 natural (4705) | AKRO-PLASTIC GmbH | PK-Aliphatic | AKROTEK® |