RTP ESD C 2580
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eHOqgN_RTP-ESD-C-2580.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. ESD 2580 Series materials are polycarbonate/ABS alloy with carbon fiber added for electrical conductivity. These materials have excellent static dissipation characteristics, are non-sloughing and are available in a wide range of colors. ESD A 2580 is st |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.15 - 0.25 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7580 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 110 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 6890 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 159 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 530 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 129 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+6 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+3 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm, Values per RTP Company testing.) | HB | UL 94 |
| Additional Information |
|---|
| Molding Shrinkage, Linear-Flow, ASTM D955, 3.175mm: 1.5-2.5mm/mStatic Decay, FTMS-4046.1, Mil B-81705C: <2.0 secondsVolume Resistivity, ASTM D257: <10E3 ohm-cmSurface Resistivity, ASTM D257: <10E6 ohm/sq |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 232 - 288 | °C | |
| Middle Temperature | 232 - 288 | °C | |
| Front Temperature | 232 - 288 | °C | |
| Mold Temperature | 71.1 - 98.9 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen RP241R | LyondellBasell Industries | PP Random Copolymer | Moplen |
| MORETEC™ V-0398CN | Prime Polymer Co., Ltd. | LLDPE | MORETEC™ |
| alphalon™ E 40 LN | Grupa Azoty ATT Polymers GmbH | Nylon 6 | alphalon™ |
| Halene H Y5401 | Haldia Petrochemicals Ltd. | HDPE | Halene H |
| Latilub 66-15T G/30 | LATI S.p.A. | Nylon 66 | Latilub |