IROGRAN® A 85 P 4394
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Huntsman Corporation |
| Trademark: | IROGRAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eGXpbg_IROGRAN-A-85-P-4394.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
IROGRAN A 85 P 4394 is a high performance polyether based thermoplastic polyurethane intended for extrusion and injection moulding applications. IROGRAN A 85 P 4394 is part of the HUNTSMAN technical extrusion product range and offers a specially designed, flexible material with a broad processing window particularly suitable for the preparation of tubing, cable jacketing and technical mouldings. PERFORMANCE FEATURES
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.12 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/21.6 kg) | 55.0 | cm³/10min | |
| Molding Shrinkage - Flow (Injection Molded) | 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shore A, Injection Molded | 85 | ||
| Shore D, Injection Molded | 36 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion 2 | 25 | mm³ | ISO 4649 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| TMA 3 | Internal Method | ||
| High : 635.0 µm | 170 | °C | |
| Low : 635.0 µm | 150 | °C |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 4 | ASTM D412, DIN 53504 | ||
| 100% Strain | 7.00 | MPa | |
| 300% Strain | 12.0 | MPa | |
| Tensile Strength 5 | |||
| Break | 35.0 | MPa | ASTM D412 |
| Break | 45.0 | MPa | DIN 53504 |
| Tensile Elongation 6 | |||
| Break | 610 | % | ASTM D412 |
| Break | 640 | % | DIN 53504 |
| Tear Strength 7 | |||
| -- | 101 | kN/m | ASTM D624 |
| -- | 60 | kN/m | ISO 34-1 |
| Compression Set 8 | ASTM D395, ISO 815 | ||
| 23°C, 24 hr | 20 | % | |
| 70°C, 24 hr | 40 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 to 110 | °C | |
| Hot Air Dryer | 80.0 to 90.0 | °C | |
| Drying Time | |||
| -- | 3.0 | hr | |
| Hot Air Dryer | 3.0 | hr | |
| Dew Point | -30.0 | °C | |
| Rear Temperature | 175 to 210 | °C | |
| Middle Temperature | 175 to 210 | °C | |
| Front Temperature | 175 to 210 | °C | |
| Nozzle Temperature | 200 to 210 | °C | |
| Processing (Melt) Temp | 190 to 205 | °C | |
| Mold Temperature | 20.0 to 70.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 3.0 | hr | |
| Hopper Temperature | 25.0 to 40.0 | °C | |
| Cylinder Zone 1 Temp. | 160 to 200 | °C | |
| Cylinder Zone 2 Temp. | 160 to 200 | °C | |
| Cylinder Zone 3 Temp. | 160 to 200 | °C | |
| Cylinder Zone 4 Temp. | 160 to 200 | °C | |
| Cylinder Zone 5 Temp. | 160 to 200 | °C | |
| Adapter Temperature | 175 to 200 | °C | |
| Die Temperature | 175 to 205 | °C |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | Injection Molded |
| 3 . | Extruded Film |
| 4 . | Injection Molded |
| 5 . | Injection Molded |
| 6 . | Injection Molded |
| 7 . | Injection Molded |
| 8 . | Injection Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® EME-6710HL | Sumitomo Bakelite Co., Ltd. | Epoxy | Sumikon® |
| VITAMIDE® AR39GY6599 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| New-prene™ 8180B | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| Elastron® V V101.A90.B | Elastron USA, Inc. | TPV | Elastron® V |
| POLYCASA® HIPS Glossy/Matt | Polycasa | PS (HIPS) | POLYCASA® |