Kepital® FC2020D
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepital® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eFCHt4_Kepital-FC2020D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A medium-high viscosity grade for general injection molding. It was modified with electrically conductive carbon fiber, and so suitable for parts requiring conductive property and high stiffness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.45 | g/cm³ | ASTM D792 |
| -- | 1.46 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 5.5 | g/10 min | ASTM D1238 |
| -- | 5.5 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 2.00 mm | 0.40 | % | ASTM D955 |
| 3.00 mm | 0.40 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.36 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C | 123 | MPa | ASTM D638 |
| Yield, 23°C | 140 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break, 23°C | 1.0 | % | ASTM D638 |
| Break, 23°C | 1.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 13500 | MPa | ASTM D790 |
| -- | 16000 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 165 | MPa | ASTM D790 |
| -- | 210 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 44 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed | 164 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 163 | °C | ISO 75-2/A |
| Peak Melting Temperature | 165 | °C | ASTM D3418 |
| CLTE - Flow (20 to 80°C) | 1.5E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec (0.800 mm) | 50.0 | °C | UL 746 |
| RTI Imp (0.800 mm) | 50.0 | °C | UL 746 |
| RTI Str (0.800 mm) | 50.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+2 | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | 1.0E+2 | ohms·cm | ASTM D257, IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Michiflex E9287A | API Polymers, Inc. | TPV | Michiflex |
| SCHULAMID® 6 GBF 3310 HI H LS | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| Titalon® 2200MS | Titan Plastics Compounds Co., Ltd. | Nylon 66 | Titalon® |
| Osterlene® HE-3.5-3-stg | Osterman & Company | PS (HIPS) | Osterlene® |
| Plaslube® PC / PBT IM 5230 | Techmer Engineered Solutions | PC+PBT | Plaslube® |