AKROMID® A3 GM 20/10 4 WIT black (4529)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eEeaBO_AKROMID-A3-GM-20-10-4-WIT-black-4529-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 GM 20/10 4 WIT black (4529) is a 20% glass fibre reinforced and 10% glass bead filled, hydrolysis/chemical stabilised polyamide 6.6 with good surface and low warpage. Applications are engineering parts, which are produced by water injection technology. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.36 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 6.00 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.40 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 2.0 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flexural Strain at Break 1 | 4.6 | 7.5 | % | ISO 178 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 30 | -- | % | ISO 1172 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8200 | 5200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 175 | 100 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.7 | 12 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 7600 | 5200 | MPa | ISO 178 |
| Flexural Stress 3 | 260 | 170 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 7.0 | 6.5 | kJ/m² | |
| 23°C | 9.0 | 9.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 50 | 48 | kJ/m² | |
| 23°C | 65 | 80 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 260 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 240 | -- | °C | ISO 75-2/A |
| Melting Temperature 4 | 262 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP PP PPC3TF1.5UV | Washington Penn Plastic Co. Inc. | PP Impact Copolymer | WPP PP |
| Xuchuan XCA-RS45A | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| ADEKA ED-502 | Adeka Corporation | Epoxy | ADEKA |
| Durethan® B 35 FA 000000 | LANXESS Corporation | Nylon 6 | Durethan® |
| RTP 299 D X 130507 A | RTP Company | Nylon 612 | RTP |