Lotader® LX4110

Category:	EAA , Ethylene Acrylic Acid Copolymer
Manufacturer:	Arkema
Trademark:	Lotader®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	eEI7Lw_Lotader-LX4110.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

LOTADER® LX4110 is a random terpolymer of ethylene, acrylic ester and maleic anhydride, polymerized by high-pressure autoclave process.

Applications
LOTADER® LX4110 is a versatile adhesive for extrusion coating or lamination, designed as:

Concentrate to be used in dry blend with LDPE. LOTADER® LX4110 improves adhesion of LDPE on aluminium foils, metallized or primerized films.

Ready for use resin to be used pure. LOTADER® LX4110 gives excellent adhesion on substrates likes aluminium foil, metallized plastics, paper, board, PE and some plastic films like BOPP.

General Information
Features	Autoclavable Good Adhesion Good Thermal Stability High Melt Stability Low Neck-In Terpolymer
Uses	Adhesives Coating Applications Film Laminates Plastics Modification
Processing Method	Extrusion Coating Laminating

Physical	Nominal Value	Unit	Test Method
Density	0.940	g/cm³	ISO 1183, ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	5.0	g/10 min	ASTM D1238, ISO 1133
Ethyl Acrylate Content	5.0	wt%
Maleic Anhydride Content	3.0	wt%

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, 15 sec, Compression Molded)	46		ASTM D2240, ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Break, Compression Molded)	11.0	MPa	ASTM D638, ISO 527-2
Tensile Elongation (Break, Compression Molded)	650	%	ASTM D638, ISO 527-2
Flexural Modulus (Compression Molded)	140	MPa	ASTM D790, ISO 178

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	78.0	°C	ISO 306/A, ASTM D1525 ¹
Melting Temperature	105	°C	ISO 11357-3

Note Message
1 .	Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
POPELEN QHCA-352M	Lotte Chemical Corporation	PP Impact Copolymer	POPELEN
SAXALEN™ PPC339T20	SAX Polymers	PP Copolymer	SAXALEN™
Multi-Flex® TPE D4107	Multibase, A Dow Corning Company	TPE	Multi-Flex® TPE
ColorRx® PA-0500NB	LTL Color Compounders, Inc.	PC+ABS	ColorRx®
POLYCOMPO PE 1300J	POLYCOMPO Co.,Ltd.	HDPE	POLYCOMPO PE