TOTAL Polyethylene HDPE XT10 N
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eDISWW_TOTAL-Polyethylene-HDPE-XT10-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TOTAL Polyethylene XT10 N is a High Density (HMW) Polyethylene material. It is available in Asia Pacific or North America for pipe extrusion. Important attributes of TOTAL Polyethylene XT10 N are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.949 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 7.5 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Compression Molded) | > 24.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, Compression Molded) | > 800 | % | ASTM D638 |
| Flexural Modulus - 2% Secant (Compression Molded) | 1030 | MPa | ASTM D790 |
| Hydrostatic Design Basis | ASTM D2837 | ||
| 23°C | 11.0 | MPa | |
| 60°C | 6.89 | MPa | |
| Notch Pipe Test | > 20.8 | day | ISO 13479 |
| Resistance to Rapid Crack Propagation, Pc (0°C) | > 12.0 | bar | ISO 13477 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | 78 | °C | ASTM D648 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cell Classification | 445576 445574 | ASTM D3350 | |
| Minimum Required Strength | 10.0 | MPa | ISO 9080 |
| PENT - Compression Molded | > 5000 | ASTM F1473 | |
| Pipe Test Category | C3 | ASTM D2239 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm, Compression Molded) | 430 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -118 | °C | ASTM D746 |
| Vicat Softening Temperature | 124 | °C | ASTM D1525 |
| Peak Melting Temperature | 131 | °C | ASTM D3417 |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696 |
| Note Message | |
|---|---|
| 1 . | Type IV, 51 mm/min |
| 2 . | Type IV, 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP692D | Southern Polymer, Inc. | LLDPE | PRIMALENE |
| Borealis PE MA8200 | Borealis AG | LDPE | Borealis PE |
| Daplen™ EE109AE | Borealis AG | PP, Unspecified | Daplen™ |
| Kumho SAN SAN 335T | Korea Kumho Petrochemical Co., Ltd. | SAN | Kumho SAN |
| POLYfill PP EIP2012 F | Polykemi AB | PP, Unspecified | POLYfill |